The development of electrocatalysts for energy conversion and storage devices is of paramount importance to promote sustainable development. Among the different families of materials, catalysts based on transition metals supported on a nitrogen-containing carbon matrix have been found to be effective catalysts toward oxygen reduction reaction (ORR) and hydrogen evolution reaction (HER) with high potential to replace conventional precious metal-based catalysts. In this work, we developed a facile synthesis strategy to obtain a Fe-N-C bifunctional ORR/HER catalysts, involving wet impregnation and pyrolysis steps. Iron (II) acetate and imidazole were used as iron and nitrogen sources, respectively, and functionalized carbon black pearls were used as conductive support. The bifunctional performance of the Fe-N-C catalyst toward ORR and HER was investigated by cyclic voltammetry, rotating ring disk electrode experiments, and electrochemical impedance spectroscopy in alkaline environment. ORR onset potential and half-wave potential were 0.95 V and 0.86 V, respectively, indicating a competitive performance in comparison with the commercial platinum-based catalyst. In addition, Fe-N-C had also a good HER activity, with an overpotential of 478 mV @10 mAcm−2 and Tafel slope of 133 mVdec−1, demonstrating its activity as bifunctional catalyst in energy conversion and storage devices, such as alkaline microbial fuel cell and microbial electrolysis cells.

In this work, we synthesized new materials based on Fe(II) phthalocyanine (FePc), urea and carbon black pearls (BP), called Fe-N-C, as electrocatalysts for the oxygen reduction reaction (ORR) in neutral solution. The electrocatalysts were prepared by combining ball-milling and pyrolysis treatments, which affected the electrochemical surface area (ECSA) and electrocatalytic activity toward ORR, and stability was evaluated by cyclic voltammetry and chronoamperometry. Ball-milling allowed us to increase the ECSA, and the ORR activity as compared to the Fe-N-C sample obtained without any ball-milling. The effect of a subsequent pyrolysis treatment after ball-milling further improved the electrocatalytic stability of the materials. The set of results indicated that combining ball-milling time and pyrolysis treatments allowed us to obtain Fe-N-C catalysts with high catalytic activity toward ORR and stability which makes them suitable for microbial fuel cell applications.