To improve the hydrogen storage properties of Mg/MgH 2 , a Ni and TiO 2 co-doped reduced graphene oxide [(Ni-TiO 2)@rGO] nanocomposite is synthesized by a facile impregnation method and introduced into Mg via ball milling. The results demonstrated that the dispersive distribution of Ni and TiO 2 with a particle size of 20-200 nm in the reduced graphene oxide matrix led to superior catalytic effects on the hydrogen storage properties of Mg-(Ni-TiO 2)@rGO. The initial hydrogenation/dehydrogenation temperature for Mg-(Ni-TiO 2)@rGO decreased to 323/479 K, 75/84 K lower than that of the additive-free sample. The hydrogen desorption capacity of the Mg-(Ni-TiO 2)@rGO composite released 1.47 wt.% within 120 min at 498 K. When the temperature was increased to 523 K, the hydrogen desorption capacity increased to 4.30 wt.% within 30 min. A hydrogenation/dehydrogenation apparent activation energy of 47.0/99.3 kJ•mol −1 was obtained for the Mg-(Ni-TiO 2)@rGO composite. The improvement in hydrogenation and dehydrogenation for the Mg-(Ni-TiO 2)@rGO composite was due to the reduction of the apparent activation energy by the catalytic action of (Ni-TiO 2)@rGO.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.