No abstract

Environmental pollution caused by CO2 releasing from the production of cement is a great challenge for the construction industry and has triggered exploration into more sustainable alternatives. Geopolymer Concrete (GPC) is a potential sustainable solution that does not involve the use of cement as a binder. GPC is produced by mixing the alumino-silicate source materials such as fly-ash with alkali activators such as potassium hydroxide (KOH) and potassium silicate (K2SiO3). Unlike Ordinary Portland Concrete (OPC), the characteristics of GPC depend on the precursor materials and therefore vary for different mixes. Consequently, corrosion behavior needs to be evaluated separately for individual mixes. This has narrowed the scope of existing published work on corrosion behavior of GPC. In this study, GPC and OPC specimens were prepared and exposed to accelerated corrosion exposure. Half-cell potential and linear polarization resistance were used to evaluate the corrosion rate in GPC and OPC. Under accelerated conditions, the corrosion rate of the GPC specimens was between 10 µm/year and 20 µm/year exhibiting a moderate to high rate of corrosion. Meanwhile, the corrosion rate of the OPC specimens was between 40 µm/year and 60 µm/year indicating a very high corrosion activity. It can be concluded that GPC has a higher resistance to chloride-induced corrosion; with a low corrosion rate and lower mass loss percentage, compared to OPC.

Repairing concrete structures costs billions of dollars every year all around the globe. For overcoming durability concerns and creating enduring economical structures, chemical admixtures, as a unique solution, have recently attracted a lot of interest. As permeability of a concrete structure is considered to play a significant role in its durability, Permeability Reducing Admixtures (PRA) is one of the ideal solutions for protecting structures exposed to water and waterborne chemicals. Different products have been developed to protect concrete structures against water penetration, which, based on their chemistry, performance, and functionality, have been categorized into PRA. As it has previously been tested by authors and proven to be a promising solution, a hydrophilic Crystalline Waterproofing Admixtures (CWA) has been considered for this study. This paper aims to investigate how this product affects concrete’s overall freeze–thaw resistance, self-sealing, and corrosion resistance. Various testing methods have been utilized to examine the performance of CWA mixtures, including the linear polarization resistance, resonance frequency testing, half-cell potential, and self-sealing test. The reinforcement corrosion potential and rate measurements indicated superior performance for CWA-treated samples. After being exposed to 300 freeze–thaw cycles, concrete mixes containing CWA—even non-air-entrained ones—showed a Durability Factor (DF) of more than 80% with no signs of failure, while non-air-entrained control samples indicated the lowest DF (below 60%) but the greatest mass loss. The major causes are a reduction in solution permeability and lack of water availability in the concrete matrix—due to the presence of CWA crystals. Furthermore, evidence from the self-sealing test suggests that CWA-treated specimens can seal wider cracks and at a faster rate.

Geopolymer Concrete (GPC) as a cement-less construction material has attracted worldwide attention due to its lower carbon footprint. There are numerous studies reported on GPC made using different by-products including fly-ash. However, since the use of bottom-ash is comparatively limited, making potassium-based GPC using this waste can be an alternative to Portland Cement Concrete (PCC). In this study, two methods of accelerated curing were used to determine the influence of elevated temperature on the compressive strength of GPC, composed of 50% bottom-ash and 50% fly-ash. GPC specimens were cured using various temperatures including ambient, 30 °C, 45 °C, 60 °C, and 80 °C for 24 h, all followed by 28 days of ambient curing. The highest compressive strength was obtained with steam curing at a temperature of 80 °C for a duration of 24 h. It is of great significance to evaluate elastic modulus of the concrete mixture so that the short-term rigidity of structures subjected to elongation, bending, or compression can be predicted. In this study, a longitudinal Resonant Frequency Test (RFT) as a non-destructive test (NDT) was used to calculate the elastic modulus of both GPC and a comparative PCC mix. Based on the results, PCC had higher resonant frequency (by about 1000 Hz) compared to GPC. A review of empirical models for predicting GPC’s elastic modulus showed that all of the predicted elastic modulus values were lower than experimental values.

It is well known that concrete is one of the most widely used construction materials in the world, and cement as its key constituent is partly responsible for global Carbon Dioxide (CO2) emission. Due to these reasons, high strength concrete with lower CO2 emission, and concrete with lower reliance on natural resources is increasingly popular. Geopolymer Concrete (GPC), due to its capability to minimize the consumption of natural resources, has attracted the attention of researchers. In cold regions, frost action is one of the primary GPC deterioration mechanisms requiring huge expenditures for repair and maintenance. In this regard, two types of GPC (fly-ash based GPC and bottom-ash based GPC) were exposed to the harsh freeze-thaw conditions using a standard test method. The dynamic elastic modulus of both types of GPC was determined using a Non-Destructive Test (NDT) method called Resonant Frequency Test (RFT). The results of RFT after exposing to 300 freeze-thaw cycles showed that bottom-ash based GPC has better freeze-thaw resistance than fly-ash based GPC. Moreover, in this study, the leachability of bottom-ash based GPC was also investigated to trace the heavy metals (including Si, Al, Na, Cr, Cu, Hg) using Toxicity Characteristic Leaching Procedure (TCLP) test. The results of the TCLP test showed that all of the heavy metals could be effectively immobilized into the geopolymer paste.