Here, we report the synthesis of spherical bimetal ZnCo-MOF materials by a hydrothermal rotacrystallization method and their catalytic activity on the air epoxidation of mixed biolefins enhanced by microwaves. The structural and chemical properties of the ZnCo-MOF materials were fully characterized by XRD, IR, SEM, TG, XPS, and NH 3 -TPD. The morphology of the material exhibited a three-dimensional spherical structure. From an NH 3 -TPD test of the ZnCo-MOF catalyst, it could be concluded that the Zn 0.1 Co 1 -MOF-H-150 rpm material had the highest acidic content and the strongest acidity among the catalysts synthesized by different methods, which gave the best performance in the epoxidation of mixed biolefins. The air epoxidation reaction was carried out under atmospheric pressure and microwave conditions, in the absence of any initiator or coreducing agent. Moreover, the Zn 0.1 Co 1 -MOF catalyst could be recycled six times without reducing the catalytic activity significantly, which showed the stability of spherical catalyst material under microwaves.

Biocarbon supported Ni catalysts have been prepared by facile impregnation of Ni species by microwave-heating and used for selective hydrogenation of nitrobenzene to cyclohexylamine. These catalysts were characterized by X-ray diffraction, Raman spectra, N2 sorption measurement, X-ray photoelectron spectroscopy, temperature programmed reduction of H2 and H2 temperature-programmed desorption. The morphology and particle size of catalysts were imaged by scanning electron microscope and transmission electron microscope. For the hydrogenation of nitrobenzene to cyclohexylamine, 10%Ni/CSC-II(b) exhibits the best catalytic activity to achieve 100 mol% conversion of nitrobenzene and 96.7% selectivity of cyclohexylamine under reaction conditions of 2.0 MPa H2 and 200 °C, ascribed to high dispersion of Ni species and formation of nanosized Ni particles on the support aided by microwave-heating. Thus-prepared Ni/CSC catalyst is greatly activated, in which the addition of precious metal like Rh is totally avoided.

No abstract