The color stability values after brushing may better reflect the discoloration of the esthetic restorative materials. Any color stability study model should consider the effects of toothbrushing that can remove the adsorbed colorants. The results of this study also showed that glass ionomer cements and compomers can be used in anterior restorations of children with their higher color stability than composite resins.

The bleaching with 10% hydrogen peroxide and 10% carbamide peroxide did not alter the enamel surface roughness, but when the bleaching treatment was performed combined with abrasive dentifrices, a significant increase in roughness values was observed.

No abstract

Objectives The aim was to examine the influence of short-fiber composite (SFC) core on the fracture-behavior of different types of indirect posterior restorations. In addition, the effect of thickness ratio of SFC-core to the thickness of the veneering conventional composite (PFC) on fracture-behavior of bi-structured composite restorations was evaluated. Materials and methods MOD cavities with removed palatal cusps were prepared on 90 intact molars. Five groups of direct overlay restorations (n = 10/group) were fabricated having a SFC-core (everX Flow) with various thicknesses (0, 1, 2, 3, 4 mm) and layer of surface PFC (G-aenial Anterior), remaining the thickness of the bi-structure restoration to be 5 mm. Four groups of CAD/CAM-made restorations (Cerasmart 270 and e-max CAD) were fabricated either with 2-mm layer of SFC-core or without fiber reinforcement. Intact teeth (n = 10) were used as control group. Restorations were statically loaded until fracture. Fracture patterns were evaluated visually. Data were analyzed using ANOVA (p = 0.05). Results With indirect overlay restorations, no statistically significant differences (p > 0.05) were observed in the load-bearing capacities between restorations reinforced by 2-mm SFC-core (bi-structured) and those fabricated from plain restorative materials. ANOVA displayed that direct overlay restorations made from 4-mm layer thickness of SFC-core had significantly higher load-bearing capacities (3050 ± 574 N) (p < 0.05) among all the groups tested. Conclusions Restorations (direct/indirect) combining SFC-core and a surface layer of conventional material demonstrated encouraging achievement in reference to fracture behavior. Clinical relevance The use of flowable short-fiber composite as reinforcing base with large direct and indirect restorations may result in more repairable failure.

ObjectivesThe purpose of this study was to investigate the effect of different air-polishing powders on the color stability of different types of composite resin restorative materials. Material and methodsThirty cylindrical specimens (15×2 mm) were prepared for each of 7 composite resin restorative materials. All specimens were polished with a series of aluminum oxide polishing discs (Sof-Lex). The prepared specimens of each composite resin were randomly divided into 3 groups of 10 specimens each, for control (Group-C) and two air-powder applications (Group-CP: Cavitron Prophy-Jet; Group-PS: Sirona ProSmile prophylaxis powder). A standard air-polishing unit (ProSmile Handly) was used. All specimens were air-powdered for 10 s at 4-bar pressure. The distance of the spray nosel from the specimens was approximately 10 mm and angulation of the nosel was 90º. Specimens were stored in 100 mL of coffee (Nescafe Classic) for 24 h at 37ºC. Color measurement of all specimens was recorded before and after exposure to staining agent with a colorimeter (Minolta CR-300). Color differences (∆E*) between the 2 color measurements (baseline and after 24 h storage) were calculated. The data were analyzed with a 2-way ANOVA test, and mean values were compared by the Tukey HSD test (p≤0.05). ResultsAccording to the 2-way ANOVA results, composite resin restorative materials, air-polishing powders, and their interaction were statistically significant (p<0.05) For Aelite Aesthetic Enemal, Filtek Z250, Grandio, CeramX Mono, and Quixfil composite resin restorative materials, no significant difference was observed between Group-PS and Group-CP (p>.05) and these groups demonstrated the highest ∆E* values. For Filtek Silorane and IntenS, the highest ∆E* values were observed in Group-PS. The lowest ∆E* values for all composite resin groups were observed in Group-C. When comparing the 7 composite resin restorative materials, Aelite Aesthetic Enemal demonstrated significantly less ∆E* values than the other composite resins tested. The highest ∆E* values were observed in Quixfil. ConclusionExcept for Quixfil, all control groups of composite resins that were polished Sof-Lex exhibited clinically acceptable ∆E values (<3.7). Air-polishing applications increased the color change for all composite resin restorative materials tested. Composite restorations may require re-polishing after air-polishing.