The Ti metal interdiffusion of Ti/Pt/Au gate metal stacks in 0.15-m GaAs PHEMTs subjected to high-temperature accelerated lifetest has been physically identified using scanning transmission electron microscopy. Further energy dispersive analysis with X-ray (EDX) analysis confirms the Ti diffusion into the AlGaAs Schottky barrier layer and the decrease of Schottky barrier height suggests the Ti-AlGaAs intermetallic formation, which is consistent with previous Rutherford backscattering spectroscopy/X-ray photoelectron spectroscopy studies. The Ti metal interdiffusion reduces the separation of the gate metal and InGaAs channel, thus leading to a slight Gm increase, positive shift in pinchoff voltage, and S21 increase during the preliminary portion of the lifetest. Accordingly, the Ti interdiffusion effect implies that the lifetime of GaAs PHEMTs subjected to high-temperature accelerated lifetest could be dependent upon the initial thickness of the Schottky layer underneath the gate metal.Index Terms-Focused-ion-beam (FIB), gate metal sinking, HEMT, interdiffusion, scanning transmission electron microscopy (STEM).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.