This research work reports the effect of boron micro-additions (180 and 470 ppm) on the solidification structure, magnetic properties and hot ductility behavior of an advanced low-carbon highly alloyed twinning-induced plasticity (TWIP) steel. For this purpose, three experimental TWIP steels were fabricated by melting commercial raw materials and casting into metallic molds. Solidification structure was characterized by means of optical and scanning electron microscopy techniques, and a statistical study was carried out to measure dendrite features. A vibrating sample magnetometer was used, at room temperature, to determine magnetic properties, and a X-ray diffraction analysis was performed in order to identify the related phases during magnetic measurements. Finally, the hot ductility in the as-cast condition was evaluated at 700, 900 and 1100 °C, under a constant strain rate of 0.001 s−1. The results indicate that boron micro-additions cause an overall refining solidification structure and austenitic grain size. However, as the boron content increases, segregation of this element promotes formation of ferrite and ε-martensite, leading to ferromagnetic behavior. Nonetheless, with subsequent hot- and cold-rolling, the single austenitic phase is achieved, and this behavior is eliminated. Hot tensile tests revealed that boron micro-addition is beneficial to the hot ductility behavior. The greatest influence was observed for the higher concentration of boron (470 ppm). In comparison with the steel without boron content, the reduction of area (RA) is more than the triple of the hot workability during straining at 900 °C. Thus, present results demonstrate that boron micro-addition has an excellent potential for refining dendritic microstructure and improving the hot-deformation behavior of present low-carbon highly alloyed TWIP steel.

Aluminum-based nanocomposites have been produced by mechanical milling, introducing silver nanoparticles within the matrix of a 7075 aluminum alloy using a high energy ball mill. The milled products were compacted by uniaxial load and pressure-less sintered under argon atmosphere, and finally hot extruded. Silver nanoparticles are well dispersed into the matrix of the powder particles as well as in the matrix of the extruded material. Transmission electron microscopy (TEM) analyses are used to corroborate and understand the hypothesis that second-phase particles finely and homogeneously dispersed in the matrix give greater strength to the material. In addition to the strengthening effect, the nanoparticles act like a process control agent (PCA) since the crystallite size of the nanocomposite is smaller at higher contents of nanoparticles.