In the present work, thermal fatigue in grey cast iron has been investigated by means of a numerical and an experimental approach. Temperature gradients were generated within the material by means of a testing rig specifically designed for the experiments. The temperature gradients were responsible for the formation of severe stress fields that led to the failure of the specimens after a fairly low number of cycles.Crack growth was monitored during the tests, and the microstructure and hardness of samples were analysed after failure and compared with those of untested alloy. The repeated thermal cycles at peak temperatures of 600, 700, and 800°C led to important microstructural alterations of cast iron and to a drop in material hardness. The pearlite lamellae lost their original shape and became more fragmented.Oxygen-rich regions surrounding the graphite flakes were produced by microgalvanic corrosion mechanism.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.