The compressive strength of cement paste specimens containing Bacillus pseudofirmus ATCC 700159 was investigated in order to study the self-healing ability in cement specimens. A partial replacement of bacteria suspension by 10%, 20%, 30% and 40% by weight was mixed into the cement paste before casting. At age 28 days of curing in lime water, cement paste specimens were pre-cracked by 40% of maximum compressive strength in order to make the crack allowing moisture and air to pass through. After that, these specimens were left curing in the air until 60 days prior to the compressive test. Results showed that the specimens containing bacteria had a potential to form a new compound which was created by bacteria. XRD and FTIR analysis proved that bacteria could produce carbonate ion and therefore, combined with calcium ion in cement paste becoming calcium carbonate compound. This leads to the increase in compressive strength of pre-cracked specimens where the one with 40% bacteria giving satisfactory results of self-healing cement.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.