Intergranular corrosion and intergranular stress corrosion cracking is influenced by precipitation of chromium carbides at grain boundaries and formation of chromium depletion regions. The present study focuses on understanding the carbide precipitation and subsequent sensitization in the weldments of Alloy 600 using two different welding techniques. The effect of heat input on microstructure and IGC susceptibility was measured using electrochemical reactivation test. The SEM studies were done to evaluate the presence of chromium depleted regions. The carbide was indentified to be Cr7C3 using TEM. The laser beam weldments showed an increased resistance to IGC as compared to TIG weldments.