Aim:The aim of the present study was to assess the change in physical properties (surface roughness, surface hardness and phase transformation) after surface grinding of zirconia by using three commercially available abrasives.Materials and Methods:Thirty sintered zirconia specimens were prepared and divided into three groups namely Group M (grinded using Mani Dia diamond bur standard grit), Group T (grinded using Tri Hawk diamond bur coarse grit) and Group P (grinded using Predator carbide bur). A customised assembly was used to follow a standardised protocol for surface grinding. The surface roughness, surface hardness and phase transformation was recorded before and after the grinding procedure.Statistical Analysis Used:ANOVA and Bonferroni post hoc test were used to assess the values obtained after the testing the surface roughness and surface hardness.Results:The results of the present study revealed the average values of change in surface roughness as Group M (0.44 μm) and Group T (1.235 μm) and Group P (-0.88 μm). The average values of change in surface hardness were Group T (19.578 HV), Group M (46.722 HV) and Group P (36.429 HV). The change in surface hardness was not statistically significant. There was no phase transformation seen after the grinding procedure.Clinical Significance:Carbide burs along with copious water irrigation when used to grind zirconia intra-orally produces has a polishing effect, minimal change in hardness & no phase transformation. The present study advocates the use of carbides for chair-side grinding of zirconia.

No abstract

The present study aimed to assess the efficacy of photofunctionalization on commercially available dental implant surfaces in a high-glucose environment. Discs of three commercially available implant surfaces were selected with various nano- and microstructural alterations (Group 1—laser-etched implant surface, Group 2—titanium–zirconium alloy surface, Group 3—air-abraded, large grit, acid-etched surface). They were subjected to photo-functionalization through UV irradiation for 60 and 90 min. X-ray photoelectron spectroscopy (XPS) was used to analyze the implant surface chemical composition before and after photo-functionalization. The growth and bioactivity of MG63 osteoblasts in the presence of photofunctionalized discs was assessed in cell culture medium containing elevated glucose concentration. The normal osteoblast morphology and spreading behavior were assessed under fluorescence and phase-contrast microscope. MTT (3-(4,5 Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) and alizarin red assay were performed to assess the osteoblastic cell viability and mineralization efficiency. Following photofunctionalization, all three implant groups exhibited a reduced carbon content, conversion of Ti4+ to Ti3+, increased osteoblastic adhesion, viability, and increased mineralization. The best osteoblastic adhesion in the medium with increased glucose was seen in Group 3. Photofunctionalization altered the implant surface chemistry by reducing the surface carbon content, probably rendering the surfaces more hydrophilic and conducive for osteoblastic adherence and subsequent mineralization in high-glucose environment.