AA1050 aluminum alloy was studied with symmetric and asymmetric rolling in various technological modes of rolling equipment. The rotational speeds of the rolls and the number of passes varied according to the initially foreseen scheme. Rolling of aluminum sheet alloy was carried out on an experimental - laboratory installation. The crystallographic texture before and after rolling was investigated using X-ray diffraction. X-ray analysis data was processed using MTEX MATLAB toolbox 75. The pole figures and the texture of the samples of aluminum alloy on the Euler space are given. It was shown that pole figures obtained based on X-ray analysis of samples, rolled by the traditional way, had orthorhombic symmetry, and the sample texture had typical components of traditional rolling, like Cu (copper), Su (with lower intensity) B (Brass).