The phase transition from the non-polar alpha-phase to the polar beta-phase of poly(vinylidene fluoride) (PVDF) has been investigated using micro-Raman spectroscopy, which is advantageous because it is a nondestructive technique. Films of alpha-PVDF were subjected to stretching under controlled rates at 80 degrees C, while the transition to beta-PVDF was monitored by the decrease in the Raman band at 794 cm(-1) characteristic of the alpha-phase, along with the concomitant increase in the 839 cm(-1) band characteristic of the beta-phase. The alpha-->beta transition in our PVDF samples could be achieved even for the sample stretched to twice (2x-stretched) the initial length and it did not depend on the stretching rate in the range between 2.0 and 7.0 mm/min. These conclusions were corroborated by differential scanning calorimetry (DSC) and X-ray diffraction experiments for PVDF samples processed under the same conditions as in the Raman scattering measurements. Poling with negative corona discharge was found to affect the alpha-PVDF morphology, improving the Raman bands related to this crystalline phase. This effect is minimized for films stretched to higher ratios. Significantly, corona-induced effects could not be observed with the other experimental techniques, i.e., X-ray diffraction and infrared spectroscopy.

No abstract

The poly(vinylidene fluoride), PVDF, and its copolymer poly(vinylidene fluoride‐trifluoroethylene), P(VDF‐TrFE), are of great scientific and technological interest due to their ferro, pyro, and piezelectrical properties besides chemical and thermal stability. Recently, their biocompatibility has been shown as well. Therefore, considering all this potentiality, self‐standing films of PVDF and P(VDF‐TrFE) containing corn starch and latex of natural rubber as additives were produced by compressing/annealing forming blends. This process allows one to discard the necessity of using solvents to dissolve either PVDF or P(VDF‐TrFE), which are toxic to human. The films were structurally characterized through Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), X‐ray diffraction, density, melt flow index, hardness, and thermal conductivity. The results showed that the polymers do not interact chemically with the additives leading to the formation of blends as physical mixtures where the additives are well dispersed within the blends at micrometer level. However, it was observed that the adhesion of the starch is better in the case of blends with P(VDF‐TrFE). Besides, the crystalline structures of the α‐PVDF and ferroelectric P(VDF‐TrFE) are kept in the blends. The density, hardness, melt flow index, and thermal conductivity values of the blends followed what should be expected from physical mixtures. POLYM. ENG. SCI., 2009. © 2009 Society of Plastics Engineers

Films containing different volumes of latex of natural rubber (NR) in a fixed mass of poly (vinylidene fluoride) (PVDF) powder were fabricated by compressing under annealing a mixture of both materials without using any solvent. This is an important issue keeping in mind that these films have to be used in the future as biomaterials in different applications once the solvents that are used to dissolve the PVDF become toxic to human. The films with different percentage of latex in PVDF were characterized using microRaman scattering and Fourier transform infrared absorption (FTIR) spectroscopies, thermomechanical techniques using thermogravimetry (TG), differential scanning calorimetry (DSC), dynamical-mechanical analysis (DMA) and scanning electron microscopy (SEM). The results showed that the latex of NR and PVDF do not interact chemically, leading to the formation of a polymeric blend with high thermal stability and mechanical properties suitable for applications involving bone (prostheses, for instance). Besides, the results recorded using the micro-Raman technique revealed that for a fixed amount of PVDF the higher the amount of latex in the blend, the better the miscibility between both materials.