No abstract

The effect of cobalt substitution with nickel was investigated for the Fischer–Tropsch synthesis reaction. Catalysts having different Ni/Co ratios were prepared by aqueous incipient wetness co-impregnation, characterized, and tested using a continuously stirred tank reactor (CSTR) for more than 200 h. The addition of nickel did not significantly modify the morphological properties measured. XRD, STEM, and TPR-XANES results showed intimate contact between nickel and cobalt, strongly suggesting the formation of a Co-Ni solid oxide solution in each case. Moreover, TPR-XANES indicated that nickel addition improves the cobalt reducibility. This may be due to H2 dissociation and spillover, but is more likely the results of a chemical effect of intimate contact between Co and Ni resulting in Co-Ni alloying after activation. FTS testing revealed a lower initial activity when nickel was added. However, CO conversion continuously increased with time on-stream until a steady-state value (34%–37% depending on Ni/Co ratio) was achieved, which was very close to the value observed for undoped Co/Al2O3. This trend suggests nickel can stabilize cobalt nanoparticles even at a lower weight percentage of Co. Currently, the cobalt price is 2.13 times the price of nickel. Thus, comparing the activity/price, the catalyst with a Ni/Co ratio of 25/75 has better performance than the unpromoted catalyst. Finally, nickel-promoted catalysts exhibited slightly higher initial selectivity for light hydrocarbons, but this difference typically diminished with time on-stream; once leveling off in conversion was achieved, the C5+ selectivities were similar (≈ 80%) for Ni/Co ratios up to 10/90, and only slightly lower (≈ 77%) at Ni/Co of 25/75.

No abstract

The ethanol steam reforming reaction (ESR) was investigated on unpromoted and potassium- and rubidium-promoted monoclinic zirconia-supported platinum (Pt/m-ZrO2) catalysts. Evidence from in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) characterization indicates that ethanol dissociates to ethoxy species, which undergo oxidative dehydrogenation to acetate followed by acetate decomposition. The acetate decomposition pathway depends on catalyst composition. The decarboxylation pathway tends to produce higher overall hydrogen selectivity and is the most favored route at high alkali loading (2.55 wt.% K and higher or 4.25 wt.% Rb and higher). On the other hand, decarbonylation is a significant route for the undoped catalyst or when a low alkali loading (e.g., 0.85% K or 0.93% Rb) is used, thus lowering the overall H2 selectivity of the process. Results of in situ DRIFTS and the temperature-programmed reaction of ESR show that alkali doping promotes forward acetate decomposition while exposed metallic sites tend to facilitate decarbonylation. In previous work, 1.8 wt.% Na was found to hinder decarbonylation completely. Due to the fact that 1.8 wt.% Na is atomically equivalent to 3.1 wt.% K and 6.7 wt.% Rb, the results show that less K (2.55% K) or Rb (4.25% Rb) is needed to suppress decarbonylation; that is, more basic cations are more efficient promoters for improving the overall hydrogen selectivity of the ESR process.

The low durability of Pt/C electro-catalysts in polymer electrolyte membrane fuel cells (PEMFC), e.g., as a result of carbon oxidation to CO2 in an acid medium, has been recognized as one of the most important hindrances to long-term stability. In this work, Pt electrocatalysts supported on TiO2-carbon and Vulcan carbon were prepared by the chemical vapor deposition method. The physical and electrochemical properties of Pt/TiO2-C and Pt/C electrocatalysts were investigated by the characterization techniques of XRD, TEM, CO stripping and cyclic and linear voltammetry. The prepared materials were electrochemically evaluated in the oxygen reduction reaction (ORR) in an acid medium at room temperature. The XRD results show crystalline fcc platinum formation. The mean particle size is between 2 and 4 nm with a spherical morphology. Pt/TiO2-C electrocatalysts showed a higher electrochemical active surface area and better activity results for the ORR compared with the Pt/C samples. The addition of TiO2 to the conventional Pt/C catalyst modifies the electronic properties affecting the oxygen adsorption and improving the catalytic activity for the oxygen reduction reaction.