In our paper, we have synthesized modified PEA and alkyd resin by replacing the new source of polyol (SDEA) which was confirmed by different analyses such as IR, and 1HNMR spectra. A series of conformal, novel, low-cost, and eco-friendly hyperbranched modified alkyd and PEA resins were fabricated with bio ZnO, CuO/ZnO) NPs through an ex-situ method for mechanical and anticorrosive coatings. The synthesized biometal oxides NPs and its composite modified alkyd and PEA were confirmed by FTIR, SEM with EDEX, TEM, and TGA, and can be stably dispersed into modified alkyd and PEA resins at a low weight fraction of 1%. The nanocomposite coating was also subjected to various tests to determine their surface adhesion, which ranged from (4B-5B), physico-mechanical characteristics such as scratch hardness, which improved from < 1.5 to > 2 kg, gloss (100–135) Specific gravity (0.92–0.96) and also chemical resistance test which passed for water, acid, and solvent except alkali, was poor because of the hydrolyzable ester group in the alkyd and PEA resins. The anti-corrosive features of the nanocomposites were investigated through salt spray tests in 5 wt % NaCl. The results indicate that well-dispersed bio ZnO and CuO/ZnO) NPs (1.0%) in the interior of the hyperbranched alkyd and PEA matrix improve the durability and anticorrosive attributes of the composites, such as degree of rusting, which ranged from 5 to 9, blistering size ranged from 6 to 9, and finally, scribe failure, which ranged from 6 to 9 mm. Thus, they exhibit potential applications in eco- friendly surface coatings. The anticorrosion mechanisms of the nanocomposite alkyd and PEA coating were attributed to the synergistic effect of bio ZnO and (CuO/ZnO) NPs and the prepared modified resins are highly rich in nitrogen elements, which might be regarded as a physical barrier layer for steel substrates.

Purpose This paper aims to investigate the prepared modified alkyd and poly(ester-amide) (PEA) resins as antimicrobial and insecticide binders for surface coating applications. Design/methodology/approach Salicylic diethanolamine and 4-(N, N-dimethylamino) benzylidene glutamic acid were prepared and used as new sources of polyol and dibasic acid for PEA and alkyd resins, then confirmed by: acid value, FT-IR and 1H-NMR. The coating performance of the resins was determined using measurements of physico-mechanical properties. The biological and insecticide activities of the prepared resins were investigated. Findings The tests carried out revealed that the modified PEA and alkyd enhanced both phyisco-mechanical and chemical properties in addition to the biological and insecticide activities. The results of this paper illustrate that the introduction of salicylic diethanolamine and 4-(N, N-dimethylamino) benzylidene glutamic acid within the resin structure improved the film performance and enhanced the antimicrobial activity performance of PEA and alkyd resins. Research limitations/implications The modified alkyd and PEA organic resins can be used as biocidal binders when incorporated into paint formulations for multiple surface applications, especially those that are exposed to several organisms. Originality/value Modified alkyd and PEA resins based on newly synthesized modifiers have a significant potential to be promising in the production and development of antimicrobial and insecticide paints, allowing them to function to restrict the spread of insects and microbial infection.