Considering that the processes of PEEK discoloration caused by either intrinsic or extrinsic factors require elucidation, the aim of this study was to investigate the long-term effect of the combined action of ageing and immersing solutions on the optical properties and color stability of PEEK material, related to surface processing (polishing or glazing). (2) Methods: This study aims to determine the influence of different ageing and staining protocols on optical properties, color changes, and surface roughness of a reinforced PEEK material (bioHPP, Bredent, Senden, Germany). For ageing, specimens were submitted to 5000 cycles in a 55 °C bath and a 5 °C bath filled with distilled water. For staining, thermal cycling was performed in a hot coffee bath (55 °C) and a bath filled with distilled water (37 °C) and in a cold juice bath (5 °C) and a bath filled with distilled water (37 °C). Translucency (TP) and opalescence (OP) parameters were determined, the total color change value (ΔΕ*) was calculated, specimens’ surface roughness was analyzed, and statistical analyses were performed. (3) Results: The mean TP values of the studied samples were in the interval of 1.25–3.60, which is lower than those reported for natural teeth or other aesthetic restoration materials. The OP values of PEEK were registered in the range of 0.27–0.75, being also lower than those of natural teeth or other aesthetic restoration materials. OP has a very strong positive relationship with TP. The mean registered Ra values for all subgroups were below 0.13 µm. Artificial ageing and staining in hot coffee proved to increase the roughness values. (4) Conclusions: The glazing of PEEK has a favorable effect on surface roughness and opalescence, irrespective of the artificial ageing or staining protocols. Artificial ageing damages the color stability and roughness of PEEK, regardless of surface processing, and decreases the translucency and opalescence of glazed surfaces. Immersion in hot coffee leads to perceivable discolorations.

An outstanding treatment challenge related to aesthetic monolithic materials is to mask discolored substrates in aesthetic areas. The purpose of the study is to evaluate the substrate masking ability of different resin composite materials and the influence of their association with luting agents and substrates. Five types of 2M2 HT (high translucency) resin composite materials were selected: Vita Enamic [E] and four types of nanoparticle-filled composites Lava Ultimate [L], Cerasmart [C], Shofu HC [S], and Hyramic [H]. Resin composite Vita VM LC with different shades was used for the substrates: 2M2, 3M2, and CP2. Variolink Esthetic Try-inpastes neutral, light+, and warm+ colors were chosen to simulate the luting agent color. Optical parameters (TP (translucency), CR (contrast ratio), and OP (opalesce)) and color differences ΔE (chromatic difference) were calculated. Statistical analyses were performed to evaluate the comparisons between the groups and establish correlations. TP average values for all materials were in the range of 21.49–24.53. OP average values were in the rage of 6.31–7.85. OP is moderate positive correlated to TP and CR is negative and strong correlated to TP. Related to materials, average color changes decrease as following: E > H > C > L > S. Referring to the tryin material, warm colors induce marked color changes of the restoration. The differences of the color changes determined by all studied substrates are significant. For the final aesthetic aspect of the restoration, it is essential to consider the underlying dental structure, luting agent, and restoration material as a whole unit. The masking ability of the investigated resin matrix ceramic materials materials shows differences, the best behavior demonstrated Shofu HC and Lava Ultimate. Marked color changes are related to high chroma substrates. For substrates with a darker color, the association with warm try-in pastes lead to marked color changes, but with neutral and light try-in pastes at most perceivable.

Color preservation of esthetic dental restorative materials in the oral environment represents, besides longevity, a concern, and there is still limited knowledge related to the effect of aging on the optical behavior of resin matrix ceramics. The study analyzed the finishing and thermocycling of resin matrix ceramic material surfaces, in order to assess their consequences on optical properties. Five resin matrix CAD/CAM ceramics, namely a polymer-infiltrated ceramic and four types of nanoparticle-filled resins, were selected for the study, and finished by polishing and glazing. Thermocycling was chosen as the in vitro aging method. Surface microroughness, optical and hardness evaluations were achieved before and after artificial aging. Statistical analyses were performed with IBM SPSS Statistics software at a significance value of p < 0.05. Micro-roughness values increased after thermocycling, but were kept under the clinically accepted values. The optical characteristics of resin matrix ceramics were not significantly modified by thermocycling. Values of the glazed samples became closer to those of the polished ones, after hydrothermal aging, even if the differences were insignificant. Thermocycling significantly decreased the microhardness, mainly for glazed samples. This could be the consequence of glaze removal during thermocycling, which means that glazes provide a surface protection for a limited time.

(1) Background: The purpose of this study was to evaluate the differences in terms of surface characteristics (roughness, topography, microhardness) among layers for multi-layered high translucent and super-high translucent zirconia and the influence of finishing and aging on surface characteristics and microstructure. (2) Methods: Three types of translucent multilayer zirconia were evaluated: STML (4Y-TZP); IPS e.maxZirCAD CEREC/in Lab MT Multi (4Y-TZP + 5Y-TZP); CeramillZolidfx ML (5Y-TZP). Ninety-six plate-shaped samples (32 for a material), 16mm x14mm x1mm size, were cut with a precision disc, polished on both sides with sand papers and sintered respecting the manufacturer’s protocol. Half of the specimens (16) were finished by polishing and the other half by glazing and then equally divided into one control group and one group subject to aging by autoclaving (1h, 134 °C, 0.2 MPa), resulting in four groups of eight samples, for each zirconia. The specimens were evaluated in three areas: cervical, medium, incisal-of each glazed or polished surface, before and after aging. Tests were performed to determine the surface roughness using a profilometer; the surface topography by an atomic force microscope (AFM) and a scanning electron microscope (SEM). Microhardness was recorded using a microhardness tester. Statistical analyses were performed using two-way ANOVA test, unpaired sample t-Test, paired sample t-Test (α = 0.05) and Pearson’s correlation. (3) Results: Before and after autoclaving, for glazed samples significance (p < 0.05) higher surface roughness, respectively lower microhardness in comparison with the polished group was assessed. No significant differences (p > 0.05) were reported between the three areas, on glazed or polished surfaces of a material. Although, after aging an increase in surface roughness was observed both on glazed and polished samples, statistical differences were found for STML (p < 0.05). No significant differences (p> 0.05) concerning microhardness among the same areas, on glazed and polished surfaces, recorded before and after aging, except CeramillZolidfx ML glazed samples. (4) Conclusions: For tested zirconia materials no significant differences among layers were registered regarding surface characteristics. Surface treatment (glazing or polishing) has a significant impact on surface roughness and microhardness. Both before and after aging, the surface roughness values for the glazed samples were higher than for those polished. The super translucent 4Y-TZP material was more affected by aging compared to the super-high translucent 5Y-TZP material. The combined material revealed similarities for each layer corresponding to the microstructure.

(1) Background: Considering that the appearance of a dental material is an important factor that contributes to the success of prosthetic restorations. The purpose of this study is to investigate the optical properties and color changes among the layers of three commercial zirconias, to compare the aspect of the polished and glazed surfaces before and after aging and to evaluate the effects of hydrothermal degradation on their aesthetics. (2) Methods: Forty-eight plate-shaped samples were sectioned from presintered blocks of each multilayer translucent zirconia with different Yttrium content: Ceramill Zolid fx ML (5 mol%) = CeZ, STML (4 mol%) = STM, IPS e.maxZirCAD CEREC/in Lab MT Multi (4 mol% + 5 mol%) = IPZ. The samples were sintered according to the recommendation of each manufacturer, and half (24) of them were polished and the other half (24) glazed on one of the surfaces. Each type was equally divided into one control and one aging group, and, for each material, this resulted in four groups (n = 12): polished-control, polished-autoclaved glazed-control, and glazed-autoclaved. The artificial aging was carried out with an autoclave and distilled water at 134 °C, 0.2 MPa for 1 h, and for optical parameters (TP, CR, OP) and color change (ΔE*) measurements on a black and white background in a CIE L*a*b* color system, a spectrophotometer was used. The specimens were evaluated in incisal, cervical, and medium areas on polished and glazed samples before and after the aging stage. Statistical analysis was achieved with a two-way ANOVA test, the unpaired t-test, and the paired t-test. (3) Results: Before and after aging, the mean TP values for polished samples were higher than the glazed ones. After aging, the mean TP values increased for all groups (except polished CeZ), and significant differences were reported for polished STM, IPZ. After LTD, the opalescence registered an increase for almost all groups (except polished CeZ, polished and glazed IPZ—medium area), and significant differences were reported for almost all groups (except STM—incisal, IPZ—cervical, medium areas). The levels of color change were between extremely slight to perceivable. (4) Conclusions: Optical properties of the selected multilayer zirconia were influenced by polishing and glazing as surface treatment and affected by artificial aging (CeZ the least); perceivable color changes for polished STM, IPZ were detected.