Biodegradable polymers have been widely used as scaffolding materials to regenerate new tissues. To mimic natural extracellular matrix architecture, a novel highly porous structure, which is a three-dimensional interconnected fibrous network with a fiber diameter ranging from 50 to 500 nm, has been created from biodegradable aliphatic polyesters in this work. A porosity as high as 98.5% has been achieved. These nano-fibrous matrices were prepared from the polymer solutions by a procedure involving thermally induced gelation, solvent exchange, and freeze-drying. The effects of polymer concentration, thermal annealing, solvent exchange, and freezing temperature before freeze-drying on the nano-scale structures were studied. In general, at a high gelation temperature, a platelet-like structure was formed. At a low gelation temperature, the nano-fibrous structure was formed. Under the conditions for nano-fibrous matrix formation, the average fiber diameter (160-170 nm) did not change statistically with polymer concentration or gelation temperature. The porosity decreased with polymer concentration. The mechanical properties (Young's modulus and tensile strength) increased with polymer concentration. A surface-to-volume ratio of the nano-fibrous matrices was two to three orders of magnitude higher than those of fibrous nonwoven fabrics fabricated with the textile technology or foams fabricated with a particulate-leaching technique. This synthetic analogue of natural extracellular matrix combined the advantages of synthetic biodegradable polymers and the nano-scale architecture of extracellular matrix, and may provide a better environment for cell attachment and function.

Tissue engineering has shown great promise for creating biological alternatives for implants. In this approach, scaffolding plays a pivotal role. Hydroxyapatite mimics the natural bone mineral and has shown good bone-bonding properties. This paper describes the preparation and morphologies of three-dimensional porous composites from poly(L-lactic acid) (PLLA) or poly(D,L-lactic acid-co-glycolic acid) (PLGA) solution and hydroxyapatite (HAP). A thermally induced phase separation technique was used to create the highly porous composite scaffolds for bone-tissue engineering. Freeze drying of the phase-separated polymer/HAP/solvent mixtures produced hard and tough foams with a co-continuous structure of interconnected pores and a polymer/HAP composite skeleton. The microstructure of the pores and the walls was controlled by varying the polymer concentration, HAP content, quenching temperature, polymer, and solvent utilized. The porosity increased with decreasing polymer concentration and HAP content. Foams with porosity as high as 95% were achieved. Pore sizes ranging from several microns to a few hundred microns were obtained. The composite foams showed a significant improvement in mechanical properties over pure polymer foams. They are promising scaffolds for bone-tissue engineering.

An injectable and self-healing collagen-gold hybrid hydrogel is spontaneously formed by electrostatic self-assembly and subsequent biomineralization. It is demonstrated that such collagen-based hydrogels may be used as an injectable material for local delivery of therapeutic agents, showing enhanced antitumor efficacy.