The ZnS thin films have been deposited by radio frequency magnetron sputtering at room temperature. Post-deposition rapid thermal annealing treatment was done for the films deposited at different powers ranging from 70 to 100 W. One peak is observed for as-deposited and annealed thin films at around 28.48° corresponding to the (111) reflection plane indicating a zincblende structure. The overall intensity of the peaks and the FWHM values of as-deposited films increased after annealing corresponding to the increase in crystallinity. The optical energy bandgap is found in the range of 3.24-3.32 eV. With increasing annealing temperature, the decrease in the Urbach energy values indicating a decrease in localized states which is in good agreement with the XRD results where the crystallinity increased. The surface morphology of the films seems to be composed of Nano-granules with a compact arrangement. Apparently, the grain size increases in the deposited films as annealing temperature increases. The compositional ratio attained close to the stoichiometric ratio of 1:1 after annealing. From the Hall effect measurement, the carrier concentration and mobility are found to increase after annealing. The high carrier concentration and mobility also comply with structural and optical analysis. Best results are found for the film annealed at 400 °C deposited at 90 W.
In this paper, we reported the extraction process of five different flowering plants utilizing different dye extraction methods and solvents (ethanol and water) to choose the best dye removal process. The FTIR spectra revealed the presence of several clear functional groups for all five natural dyes. The analytical studies such as UV spectroscopy, column chromatography, and vacuum evaporation were performed to isolate the dyes from their solutions. The UV-Vis studies on the pigments of flower extracts indicated broad absorption peaks in the visible region including clear bandgaps. Among the studied pigments, Alternanthera ficoidea showed the lowest direct bandgap of 1.69 eV and an Urbach energy value of 6.33 meV. The dye extraction yield rate improvement was extended from 11.7 to 24.7% (water solvent) and 11.3-32.4% (ethanol solvent). Throughout the studies, it was observed that ethanol produced a better extraction for organic dyes than water as a solvent. Aging studies revealed that all the dyes at the room temperature showed better stability with minor changes in the observed optical parameters in oxygen-rich conditions; however, these parameters have shown significant variations at a 60 C temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.