Terminal sterilization of bone allografts by gamma radiation is often essential prior to their clinical use to minimize the risk of infection and disease transmission. While gamma radiation has efficacy superior to other sterilization methods it also impairs the material properties of bone allografts, which may result in premature clinical failure of the allograft. The mechanisms by which gamma radiation sterilization damages bone tissue are not well known although there is evidence that the damage is induced via free radical attack on the collagen. In the light of the existing literature, it was hypothesized that gamma radiation induced biochemical damage to bone's collagen that can be reduced by scavenging for the free radicals generated during the ionizing radiation. It was also hypothesized that this lessening of the extent of biochemical degradation of collagen will be accompanied by alleviation in the extent of biomechanical impairment secondary to gamma radiation sterilization. Standardized tensile test specimens machined from human femoral cortical bone and specimens were assigned to four treatment groups: control, scavenger treated-control, irradiated and scavenger treated-irradiated. Thiourea was selected as the free radical scavenger and it was applied in aqueous form at the concentration of 1.5 M. Monotonic and cyclic mechanical tests were conducted to evaluate the mechanical performance of the treatment groups and the biochemical integrity of collagen molecules were assessed by sodium dodecyl sulfate-polyacrylamide gel electrophoresis.The native mechanical properties of bone tissue did not change by thiourea treatment only. The effect of thiourea treatment on mechanical properties of irradiated specimens were such that the post-yield energy, the fracture energy and the fatigue life of thiourea treated-irradiated treatment group were 1.9-fold, 3.3-fold and 4.7-fold greater than those of the irradiated treatment group, respectively. However, the mechanical function of thiourea treated and irradiated specimens was not to the level of unirradiated controls. The damage occurred through the cleavage of the collagen backbone as revealed by SDS PAGE analysis. Irradiated specimens did not exhibit a noteworthy amount of intact a-chains whereas those irradiated in the presence of thiourea demonstrated intact a-chains. Results demonstrated that free radical damage is an important pathway of damage, caused by cleaving the collagen backbone. Blocking the activity of free radicals using the scavenger thiourea reduces the extent of damage to collagen, helping to maintain the mechanical strength of sterilized tissue. Therefore, free radical scavenger thiourea has the potential to improve the functional life-time of the allograft component following transplantation.

Cortical bone grafts are utilized frequently for skeletal reconstruction, spinal fusion and tumor surgery. Due to its efficacy and convenience terminal sterilization by gamma radiation is often essential to minimize disease transmission and infection. However, the impairment in the material properties of bone tissue secondary to gamma radiation sterilization is a concern since the mechanical functionality of a bone graft is of primary importance. While the extent of this impairment is well investigated for monotonic loading conditions, there does not seem to exist any information on the effects of gamma radiation sterilization on cortical bone's fatigue properties, the physiologically relevant mode of loading. In this study we investigated the degradation in the high-cycle and lowcycle tensile fatigue lives of cortical bone tissue secondary to gamma radiation sterilization at a dose of 36.4 kGy which approximately falls in the higher end of the standard dose range used in tissue banking. The high-cycle and the low-cycle fatigue tests were conducted under load control at initial strain levels of 0.2% and 0.4%, respectively. Monotonic tensile tests were also conducted to compare the impairment of fatigue properties with the impairment of monotonic properties. Results demonstrated that the impairment in both the high-cycle and the low-cycle fatigue lives were two orders of magnitude following sterilization, a change much more pronounced than that observed for monotonic loading. In conclusion, the results suggest that the impairment of the mechanical function of gamma radiation sterilized allografts is even worse in fatigue than monotonically. Therefore, grafts should be designed to minimize functional strains and avoid stress raisers to prevent premature fatigue failures.