Changes in structure of dibutyrylchitin fibres in the process of chitin regeneration Summary-Dibutyrylchitin (DBCH) fibres were formed from the solution of the polymer in and anhydrous ethyl alcohol. The fibres obtained were then treated with a 5 % aq. potassium hydroxide solution at temperatures ranging from 20 o C to 90 o C. The process of chitin regeneration was carried out gradually and its rate depended on the temperature. High temperature alkaline treatment causes that the transformation of DBCH fibres into fibres of regenerated chitin becomes more effective. Molecular and supermolecular structural changes of fibres were examined by wide angle X-ray diffraction (WAXS), FT-IR spectroscopy and Raman spectroscopy. The obtained diffractograms were analyzed using Hindeleh and Johnson method and the computer programme "Optifit" in which Rosenbrock method was applied. The analysis of WAXS diffraction patterns showed that the curve obtained for regenerated chitin is similar to the curve obtained for the native krill chitin. The analysis of FT-IR spectra proved that as a result of hydrolysis of DBCH fibres the transformation of DBCH into chitin took place and chemical structure of the obtained chitin was almost the same as the structure of the initial native chitin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.