It is well documented that an important cause of osteolysis and subsequent loosening of replacement hip joints is polyethylene wear debris. To avoid this, interest has been renewed in metal-on-metal and ceramic-on-ceramic prostheses. Various workers have assessed the lubrication modes of different joints by measuring the friction at the bearing surfaces, using different lubricants. Measurements of friction factors of a series of hip prostheses were undertaken using carboxymethyl cellulose (CMC) fluids, silicone fluids, synovial fluid and different concentrations of bovine serum as the lubricant. The experimental results were compared with theoretical predictions of film thicknesses and lubrication modes. A strong correlation was observed between experiment and theory when employing CMC fluids or silicone fluids as the lubricant. Mixed lubrication was found to occur in the metal-on-metal (CoCrMo/CoCrMo) joints with all lubricants at a viscosity within the physiological range. This was also the case for the metal-on-plastic (CoCrMo/ultra-high molecular weight polyethylene) joints. The ceramic-on-ceramic (Al2O3/Al2O3) joints, however, exhibited full fluid film lubrication with the synthetic lubricants but mixed lubrication with the biological lubricants. Employing a biological fluid as the lubricant affected the friction to varying degrees when compared with the synthetic lubricants. In the case of the ceramic-on-ceramic joints it acted to increase the friction factor tenfold; however, for the metal-on-metal joints, biological fluids gave slightly lower friction than the synthetic lubricants did. This suggests that, when measuring friction and wear of artificial joints, a standard lubricant should be used.

Use policyThe full-text may be used and/or reproduced, and given to third parties in any format or medium, without prior permission or charge, for personal research or study, educational, or not-for-prot purposes provided that:• a full bibliographic reference is made to the original source • a link is made to the metadata record in DRO • the full-text is not changed in any way The full-text must not be sold in any format or medium without the formal permission of the copyright holders.Please consult the full DRO policy for further details. Abstract: It is well documented that hard bearing combinations show a running-in phenomenon in vitro and there is also some evidence of this from retrieval studies. In order to investigate this phenomenon, five Birmingham hip resurfacing devices were tested in a hip wear simulator. One of these (joint 1) was also tested in a friction simulator before, during, and after the wear test and surface analysis was conducted throughout portions of the testing. The wear showed the classical running in with the wear rate falling from 1.84 mm3 per 106 cycles for the first 106 cycles of testing to 0.24 mm3 per 106 cycles over the final 2×106 cycles of testing. The friction tests suggested boundary lubrication initially, but at 1×106 cycles a mixed lubrication regime was evident. By 2×106 cycles the classical Stribeck curve had formed, indicating a considerable contribution from the fluid film at higher viscosities. This continued to be evident at both 3×106 and 5×106 cycles. The surface study complements these findings.Keywords: metal-on-metal resurfacing, wear, running in, lubrication, simulator study INTRODUCTIONlarge-diameter metal-on-metal joints were not initially fully fluid film lubricated and friction tests on other types of metal-on-metal joint have revealed Early, small-diameter (less than 32 mm) metal-onmetal hip joints were prone to premature failure [1], lower friction factors post-wear than initially [8], pointing towards more favourable lubrication after although some examples are known to have been in place successfully for up to 20 years [2, 3]. This wear testing. It has also been noted that the average linear wear rate (microns per year) for retrieved suggests there is a favourable tribological condition in some cases, although not in the majority of cases metal-on-metal joints is lower for joints with a longer survivorship, indicating that this wearing-in phase is for the early designs of metal-on-metal joints. New-generation larger-diameter metal-on-metal hip also likely to occur in vivo [12]. All this suggests that the articulating surfaces run in during early stages of joints have been more successful in the midterm [4, 5] although longer-term clinical results are not yet the wear test, and that this improves the lubrication conditions and hence lowers the wear even further available.Hard bearing joints often show a wearing-in period as the tests progress. during simulator wear tests [6][7][8][9][10], where the initial wear rates are higher than the steady state wear...

It is well known that a reduction in the volume of wear produced by articulating surfaces in artificial joints is likely to result in a lower incidence of failure due to wear particle induced osteolysis. Therefore, new materials have been introduced in an effort to produce bearing surfaces with lower, more biologically acceptable wear. Polyetheretherketone (PEEK-OPTIMA) has been successfully used in a number of implant applications due to its combination of mechanical strength and biocompatibility. Pin-on-plate wear tests were performed on various combinations of PEEK-OPTIMA and carbon fibre reinforced PEEK-OPTIMA (CFR-PEEK) against various CoCrMo alloys to assess the potential of this material combination for use in orthopaedic implants. The PEEK/low carbon CoCrMo produced the highest wear. CFR-PEEK against high carbon or low carbon CoCrMo provided low wear factors. Pin-on-plate tests performed on ultra-high molecular weight polyethylene (UHMWPE) against CoCrMo (using comparable test conditions) have shown similar or higher wear than that found for CFR-PEEK/CoCrMo. This study gives confidence in the likelihood of this material combination performing well in orthopaedic applications.

The tribological testing of artificial hip and knee joints in the laboratory has been ongoing for several decades. This work has been carried out in an attempt to simulate the loading and motion conditions applied in vivo and, therefore, the potential for the success of the joint. However, several different lubricants have been used in these tests. The work documented in this paper compares results obtained using different lubricants and makes suggestions for future work. Hip joints and knee joints of different material combinations were tested in a friction simulator to determine their friction and lubrication properties. Both carboxymethyl cellulose (CMC) fluids and bovine serum (with CMC fluids added) were used as the lubricants. These were prepared to various viscosities to produce the Stribeck plots. Human synovial fluid, of just one viscosity, was used as the lubricant with some of the joints to give a true comparison with physiological lubricants. The results showed that, in most cases, the lubricant had a significant effect on the friction developed between the joint surfaces. This is thought to be due to the proteins that are present within the bovine serum adsorbing to the bearing surfaces, creating 'solid-like' films which rub together, protecting the surfaces from solid-to-solid contact. This would be beneficial in terms of wear but can either increase or decrease the friction between the contacting surfaces. It is important to simulate the conditions in vivo as closely as possible when testing these joints to try to obtain a better comparison between the joints and to simulate more accurately the way that these joints will operate in the body. In an attempt to simulate synovial fluid, bovine serum seems to be the most popular lubricant used at present. It would be beneficial, however, to develop a new synthetic lubricant that more closely matches synovial fluid. This would allow us to predict more accurately how these joints would operate long-term in vivo.

New material combinations have been introduced as the bearing surfaces of hip prostheses in an attempt to prolong their life by overcoming the problems of failure due to wear-particle-induced osteolysis. This will hopefully reduce the need for revision surgery. The study detailed here used a hip simulator to assess the volumetric wear rates of large-diameter carbon-fibre-reinforced pitch-based poly(ether-ether-ketone) (CFR-PEEK) acetabular cups articulating against alumina femoral heads. The joints were tested for 25 x 10(6) cycles. Friction tests were also performed on these joints to determine the lubrication regime under which they operate. The average volumetric wear rate of the CFR-PEEK acetabular component of 54 mm diameter was 1.16 mm(3)/10(6) cycles, compared with 38.6 mm(3)/10(6) cycles for an ultra-high-molecular-weight polyethylene acetabular component of 28 mm diameter worn against a ceramic head. This extremely low wear rate was sustained over 25 x 10(6) cycles (the equivalent of up to approximately 25 years in vivo). The frictional studies showed that the joints worked under the mixed-boundary lubrication regime. The low wear produced by these joints showed that this novel joint couple offers low wear rates and therefore may be an alternative material choice for the reduction of osteolysis.