Two different commercial refractory castables based on mullite or magnesia aggregates have been improved through addition of 0-25 wt.% nano-magnesium aluminate spinel (MA) powder. Physico-mechanical and refractory properties were tested at different firing temperatures. The phase composition, thermal analysis, and microstructure of these refractory castables were detected using X-ray diffraction (XRD), differential thermal analysis (DTA), as well as scanning electron microscope (SEM) attached with energy dispersive X-ray unit, respectively. The castable sample mix containing 10 wt.% nano-MA spinel powder was chosen as an optimum composition according to its good sintering, mechanical as well as refractory properties. *nagy2071@yahoo.com

Chemical looping combustion (CLC) is a promising solution for the next coal-fired power generation technology with inherent CO 2 separation capability. One of the critical aspects for the development of the CLC process is to develop suitable oxygen carrier (OC) particles to transfer oxygen to the fuel in the absence of air. Relevant studies have focused on active material screening, thermodynamic analysis and operational tests. This investigation was conducted on the microstructural property of OCs, to be specific, the particle porosity effect on the performance of iron-based OCs. Fe 2 O 3 , supported on Al 2 O 3 was used as the oxygen carrier. The effect of water content of the spray slurry used to produce the OC was varied to determine the influence of OC porosity on reactivity, oxygen transfer capacity and mechanical durability. A preliminary test was done to establish the minimum and maximum water percentage needed to make slurry. A process that included freeze granulation (FG), freeze drying, and calcination was used to prepare four samples of iron oxide/alumina with various water-to-solid phase ratios. A scanning electron microscope (SEM) was used to characterize the porosity of FG Fe 2 O 3 /Al 2 O 3 particles. A direct relationship was observed. A Shimpo FGE-10X force gauge was used to measure the crushing strength of selected samples. A thermogravimetric analyzer (TGA) coupled with a mass spectrometer (MS) was used to study the change in reaction rates through multiple reduction-oxidation cycles of the samples. Crystallinity of the OCs in reduced and oxidized forms were confirmed by XRD analysis.