We report the electrochemical reduction of CO2 at copper foams with hierarchical porosity. We show that both the distribution of products formed from this reaction and their faradaic efficiencies differ significantly from those obtained at smooth electropolished copper electrodes. We attribute these differences to be due to high surface roughness, hierarchical porosity, and confinement of reactive species. We provide preliminary evidence in support of these claims.

This article reports a direct chemical pathway for antioxidant deactivation on the surfaces of carbon nanomaterials. In the absence of cells, carbon nanotubes are shown to deplete the key physiological antioxidant glutathione (GSH) in a reaction involving dissolved dioxygen that yields the oxidized dimer, GSSG, as the primary product. In both chemical and electrochemical experiments, oxygen is only consumed at a significant steady-state rate in the presence of both nanotubes and GSH. GSH deactivation occurs for single- and multi-walled nanotubes, graphene oxide, nanohorns, and carbon black at varying rates that are characteristic of the material. The GSH depletion rates can be partially unified by surface area normalization, are accelerated by nitrogen doping, and suppressed by defect annealing or addition of proteins or surfactants. We propose that dioxygen reacts with active sites on graphenic carbon surfaces to produce surface-bound oxygen intermediates that react heterogeneously with glutathione to restore the carbon surface and complete a catalytic cycle. The direct catalytic reaction between nanomaterial surfaces and antioxidants may contribute to oxidative stress pathways in nanotoxicity, and the dependence on surface area and structural defects suggest strategies for safe material design.

Viologens, either as anions in solution or as pendant substituents to pyrrole, were incorporated as dopants to electrodeposited films of polypyrrole. The resulting polymer films exhibited redox activity at -0.5 V vs Ag/AgCl. The film consisting of polypyrrole with pendant viologens exhibited the best charge-discharge behavior with a maximum capacity of 55 mAh/g at a discharge current of 0.25 mA/cm(2). An anode consisting of polypyrrole (pPy) doped with viologen (V) was coupled to a cathode consisting of pPy doped with 2,2'-azino-bis(3-ethylbenzothiazoline-6-sulfonic acid) (ABTS) to yield a polymer-based battery with a cell electromotive force (emf) of 1.0 V, maximum capacity of 16 mAh/g, and energy density of 15 Wh/kg.