A cutinase from Thermomyces cellullosylitica (Thc_Cut1), hydrolyzing the synthetic polymer polyethylene terephthalate (PET), was fused with two different binding modules to improve sorption and thereby hydrolysis. The binding modules were from cellobiohydrolase I from Hypocrea jecorina (CBM) and from a polyhydroxyalkanoate depolymerase from Alcaligenes faecalis (PBM). Although both binding modules have a hydrophobic nature, it was possible to express the proteins in E. coli . Both fusion enzymes and the native one had comparable kcat values in the range of 311 to 342 s(-1) on pNP-butyrate, while the catalytic efficiencies kcat/Km decreased from 0.41 s(-1)/ μM (native enzyme) to 0.21 and 0.33 s(-1)/μM for Thc_Cut1+PBM and Thc_Cut1+CBM, respectively. The fusion enzymes were active both on the insoluble PET model substrate bis(benzoyloxyethyl) terephthalate (3PET) and on PET although the hydrolysis pattern was differed when compared to Thc_Cut1. Enhanced adsorption of the fusion enzymes was visible by chemiluminescence after incubation with a 6xHisTag specific horseradish peroxidase (HRP) labeled probe. Increased adsorption to PET by the fusion enzymes was confirmed with Quarz Crystal Microbalance (QCM-D) analysis and indeed resulted in enhanced hydrolysis activity (3.8× for Thc_Cut1+CBM) on PET, as quantified, based on released mono/oligomers.

Abstract:A new esterase from Thermobifida halotolerans (Thh_Est) was cloned and expressed in E. coli and investigated for surface hydrolysis of polylactic acid (PLA) and polyethylene terephthalate (PET). Thh_Est is a member of the serine hydrolases superfamily containing the -GxSxG-motif with 85-87% homology to an esterase from T. alba, to an acetylxylan esterase from T. fusca and to various Thermobifida cutinases. Thh_Est hydrolyzed the PET model substrate bis(benzoyloxyethyl)terephthalate and PET releasing terephthalic acid and mono-(2-hydroxyethyl) terephthalate in comparable amounts (19.8 and 21.5 mmol/mol of enzyme) while no higher oligomers like bis-(2-hydroxyethyl) terephthalate were detected. Similarly, PLA was hydrolyzed as indicated by the release of lactic acid. Enzymatic surface hydrolysis of PET and PLA led to a strong hydrophilicity increase, as quantified with a WCA decrease from 90.8° and 75.5° to 50.4° and to a complete spread of the water drop on the surface, respectively. OPEN ACCESSPolymers 2012, 4 618

g Cutinases have shown potential for hydrolysis of the recalcitrant synthetic polymer polyethylene terephthalate (PET). We have shown previously that the rate of this hydrolysis can be enhanced by the addition of hydrophobins, small fungal proteins that can alter the physicochemical properties of surfaces. Here we have investigated whether the PET-hydrolyzing activity of a bacterial cutinase from Thermobifida cellulosilytica (Thc_Cut1) would be further enhanced by fusion to one of three Trichoderma hydrophobins, i.e., the class II hydrophobins HFB4 and HFB7 and the pseudo-class I hydrophobin HFB9b. The fusion enzymes exhibited decreased k cat values on soluble substrates (p-nitrophenyl acetate and p-nitrophenyl butyrate) and strongly decreased the hydrophilicity of glass but caused only small changes in the hydrophobicity of PET. When the enzyme was fused to HFB4 or HFB7, the hydrolysis of PET was enhanced >16-fold over the level with the free enzyme, while a mixture of the enzyme and the hydrophobins led only to a 4-fold increase at most. Fusion with the non-class II hydrophobin HFB9b did not increase the rate of hydrolysis over that of the enzyme-hydrophobin mixture, but HFB9b performed best when PET was preincubated with the hydrophobins before enzyme treatment. The pattern of hydrolysis by the fusion enzymes differed from that of Thc_Cut1 as the concentration of the product mono(2-hydroxyethyl) terephthalate relative to that of the main product, terephthalic acid, increased. Small-angle X-ray scattering (SAXS) analysis revealed an increased scattering contrast of the fusion proteins over that of the free proteins, suggesting a change in conformation or enhanced protein aggregation. Our data show that the level of hydrolysis of PET by cutinase can be significantly increased by fusion to hydrophobins. The data further suggest that this likely involves binding of the hydrophobins to the cutinase and changes in the conformation of its active center. P olyethylene terephthalate (PET) is the best-known and most widespread synthetic polyester in the world. It is used for foils and bottles as well as for fibers for the textile industry (1). Recycling of PET and modification of its properties for different applications by traditional procedures involve harsh chemical and physicochemical treatments (2, 3). Enzymatic modification, particularly by cutinases, has been recognized as a powerful alternative in the past decade (4, 5) and, besides offering new avenues for PET recycling, has the additional advantage of creating a modified PET with increased dyeing efficacy and improved binding to polyvinyl chloride without altering the polymer's bulk properties (4, 5).On the other hand, enzymatic hydrolysis of PET has the inherent disadvantage of occurring at a very low rate (5, 6). The reasons for this are not yet clearly understood. The access of the active center of the cutinase to the insoluble substrate is apparently one of the rate-limiting points, because enlarging the areas around the active sites of cutinases from Fus...

Modeling and comparison of the structures of the two closely related cutinases Thc_Cut1 and Thc_Cut2 from Thermobifida cellulosilytica DSM44535 revealed that dissimilarities in their electrostatic and hydrophobic surface properties in the vicinity to the active site could be responsible for pronounced differences in hydrolysis efficiencies of polyester (i.e., PET, polyethyleneterephthalate). To investigate this hypothesis in more detail, selected amino acids of surface regions outside the active site of Thc_Cut2, which hydrolyzes PET much less efficiently than Thc_Cut1 were exchanged by site-directed mutagenesis. The mutants were expressed in E. coli BL21-Gold(DE3), purified and characterized regarding their specific activities and kinetic parameters on soluble substrates and their ability to hydrolyze PET and the PET model substrate bis(benzoyloxyethyl) terephthalate (3PET). Compared to Thc_Cut2, mutants carrying Arg29Asn and/or Ala30Val exchanges showed considerable higher specific activity and higher kcat /KM values on soluble substrates. Exchange of the positively charged arginine (Arg19 and Arg29) located on the enzyme surface to the non-charged amino acids serine and asparagine strongly increased the hydrolysis activity for 3PET and PET. In contrast, exchange of the uncharged glutamine (Glu65) by the negatively charged glutamic acid lead to a complete loss of hydrolysis activity on PET films. These findings clearly demonstrate that surface properties (i.e., amino acids located outside the active site on the protein surface) play an important role in PET hydrolysis.

A novel esterase, PpEst, that hydrolyses the co-aromatic-aliphatic polyester poly(1,4-butylene adipate-co-terephthalate) (PBAT) was identified by proteomic screening of the Pseudomonas pseudoalcaligenes secretome. PpEst was induced by the presence of PBAT in the growth media and had predicted arylesterase (EC 3.1.1.2) activity. PpEst showed polyesterase activity on both whole and milled PBAT film releasing terephthalic acid and 4-(4-hydroxybutoxycarbonyl)benzoic acid while end product inhibition by 4-(4-hydroxybutoxycarbonyl)benzoic acid was observed. Modelling of an aromatic polyester mimicking oligomer into the PpEst active site indicated that the binding pocket could be big enough to accommodate large polymers. This is the first report of a PBAT degrading enzyme being identified by proteomic screening and shows that this approach can contribute to the discovery of new polymer hydrolysing enzymes. Moreover, these results indicate that arylesterases could be an interesting enzyme class for identifications of polyesterases.Electronic supplementary materialThe online version of this article (doi:10.1007/s00253-016-7992-8) contains supplementary material, which is available to authorized users.