This contribution investigates the effects of seawater and colloidal silica (NS) in the amounts of 1, 3 and 5 wt%, respectively, on the hydration, strength development and microstructural properties of Portland cement pastes. The data reveal that seawater has an accelerating effect on cement hydration and thus a significant contribution to early strength development was observed. The beneficial effect of seawater was reflected in an improvement in compressive strength for up to 14 days of hydration, while in the 28 days compressive strength values were comparable to that of cement pastes produced with demineralized water. The combination of seawater and NS significantly promotes cement hydration kinetics due to a synergistic effect, resulting in higher calcium hydroxide (CH) production. NS can thus react with the available CH through the pozzolanic reaction and produce more calcium silicate hydrate (C-S-H) gel. A noticeable improvement of strength development, as the result of the synergistic effect of NS and seawater, was therefore observed. In addition, mercury intrusion porosimetry (MIP) tests confirmed significant improvements in microstructure when NS and seawater were combined, resulting in the production of a more compact and dense hardened paste structure. The optimal amount of NS to be mixed with seawater, was found to be 3 wt% of cement.

This study presents the results of an experimental investigation of the effects of nanosilica (NS) on the strength development, transport properties, thermal conductivity, air-void, and pore characteristics of lightweight aggregate concrete (LWAC), with an oven-dry density <1000 kg/m3. Four types of concrete mixtures, containing 0 wt.%, 1 wt.%, 2 wt.%, and 4 wt.% of NS were prepared. The development of flexural and compressive strengths was determined for up to 90 days of curing. In addition, transport properties and microstructural properties were determined, with the use of RapidAir, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM) techniques. The experimental results showed that NS has remarkable effects on the mechanical and transport properties of LWACs, even in small dosages. A significant improvement in strength and a reduction of transport properties, in specimens with an increased NS content, was observed. However, the positive effects of NS were more pronounced when a higher amount was incorporated into the mixtures (>1 wt.%). NS contributed to compaction of the LWAC matrix and a modification of the air-void system, by increasing the amount of solid content and refining the fine pore structure, which translated to a noticeable improvement in mechanical and transport properties. On the other hand, NS decreased the consistency, while increasing the viscosity of the fresh mixture. An increment of superplasticizer (SP), along with a decrement of stabilizer (ST) dosages, are thus required.

No abstract

Recently, the recycling of waste glass has become a worldwide issue in the reduction of waste and energy consumption. Waste glass can be utilized in construction materials, and understanding its effects on material properties is crucial in developing advanced materials. In this study, recycled crushed and expanded glasses are used as lightweight aggregates for concrete, and their relation to the material characteristics and properties is investigated using several approaches. Lightweight concrete specimens containing only crushed and expanded waste glass as fine aggregates are produced, and their pore and structural characteristics are examined using image-based methods, such as scanning electron microscopy (SEM), X-ray computed tomography (CT), and automated image analysis (RapidAir). The thermal properties of the materials are measured using both Hot Disk and ISOMET devices to enhance measurement accuracy. Mechanical properties are also evaluated, and the correlation between material characteristics and properties is evaluated. As a control group, a concrete specimen with natural fine sand is prepared, and its characteristics are compared with those of the specimens containing crushed and expanded waste glass aggregates. The obtained results support the usability of crushed and expanded waste glass aggregates as alternative lightweight aggregates.

No abstract