This study analysed the influence of the codeposition of SiC particles with different sizes: 50 nm, 500 nm and 5 μm, and the type of bath agitation (stirring or ultrasonic) on the electrocrystallisation of nickel coatings. The composites matrix microstructure was analysed by means of SEM, EBSD and XRD, to evaluate the grain size, crystal orientation, and internal stresses and was benchmarked against pure nickel samples electrodeposited in equivalent conditions. The codeposition of nano- and microsize particles with an approximate content of 0.8 and 4 vol.%, respectively, caused only a minor grain refinement and did not vary the dominant < 100 > crystal orientation observed in pure Ni. The internal stress was, however, increased by particles codeposition, up to 104 MPa by nanoparticles and 57 MPa by microparticles, compared to the values observed in pure nickel (41 MPa). The higher codeposition rate (11 vol.%) obtained by the addition of submicron-size particles caused a change in the grain growth from columnar to equiaxial, resulting in deposits with a fully random crystal orientation and pronounced grain refinement. The internal stress was also increased by 800% compared to pure nickel. The ultrasound (US) agitation during the deposition caused grain refinement and a selective particle inclusion prompting a decrease in the content of the particles with the larger particles. The deposits produced under US agitation showed an increase in the internal stresses, with double values compared to stirring. The increase in the deposits microhardness, from 280 HV in pure Ni to 560 HV in Ni/SiC submicron-US, was linked to the microstructural changes and particles content. Graphical abstract

This work explores the surface protection against wear provided by electroplated metal matrix composite coatings containing hard and lubricant particles. The second phase mix was selected to provide wear resistance by hardening the material and decreasing the friction coefficient. In this study, the capacity of providing wear protection by nano-SiC and self-lubrication by submicron graphite was addressed. Nickel-based composites with a dual powder mix of SiC 60 nm and graphite 400 nm, combined on a 10:10 g L−1 ratio, were produced by electrocodeposition. In addition, to better understand their synergy, mono-composites with SiC 60 nm or Graphite 400 nm with a powder load of 10 g L−1 were also produced. Pure nickel was also electrodeposited under the same conditions as a benchmark. Electron backscatter diffraction (EBSD) maps and chemical composition analysis were used to correlate the results from microhardness, wear resistance, and friction to the microstructure and particle incorporation rate. The wear rate tested by pin-on-disc decreased when the codeposition fraction and microhardness increased. Three main factors were determined to contribute to the coating hardness: Intrinsic hardness of the particle type, strengthening by grain refinement, and dispersion strengthening. The composites containing SiC provided the best wear protection due to the highest microhardness and grain refinement.