A bis(acyl)phosphane oxide (BAPO) photoinitiator was conveniently synthesized in an efficient one-pot process. It shows excellent dispersibility in water, good storage stability, and high photo-reactivity in 3D printing of hydrogels under visible-light irradiation (460 nm).

Long-chain branching (LCB) is known as a suitable method to increase the melt strength behavior of linear polypropylene (PP), which is a fundamental weakness of this material. This enables the modification of various properties of PP, which can then be used—in the case of PP recyclates—as a practical “upcycling” method. In this study, the effect of five different peroxides and their effectiveness in building LCB as well as the obtained mechanical properties were studied. A single screw extruder at different temperatures (180 and 240 °C) was used, and long-chain branched polypropylene (PP-LCB) was prepared via reactive extrusion by directly mixing the peroxides. The peroxides used were dimyristyl peroxydicarbonate (PODIC C126), tert-butylperoxy isopropylcarbonate (BIC), tert-Butylperoxy 2-ethylhexyl carbonate (BEC), tert-amylperoxy 2-ethylhexylcarbonate (AEC), and dilauroyl peroxide (LP), all with a concentration of 20 mmol/kg. The influence of the temperature on the competitive prevalent reactions of degradation and branching was documented via melt mass-flow rate (MFR), rheology measurements, and gel permeation chromatography (GPC). However, via extensional rheology, strain hardening could be observed in all cases and the mechanical properties could be maintained or even improved. Particularly, PODIC C126 and LP signaled a promising possibility for LCB in this study.

The influence of reactive processing, non reactive and reactive copolymers on immiscible polypropylene (PP)–polystyrene (PS) blends with varying PS concentrations (10 wt.% and 25 wt.%) was evaluated by mechanical (tensile and tensile impact), rheological (melt flow rate, extensional and dynamic rheology) and morphological (scanning electron microscopy) analysis. As an extended framework of the study, the creation of a link to industrial applicable processing conditions as well as an economically efficient use of compatibilzing agent were considered. For radical processed blends, a high improvement in melt strength was observed while non reactive copolymers exhibited a pronounced increase in toughness and ductility correlated with overall best phase homogeneity. Conversely, the influence of the reactive copolymer was quite different for the varied PS concentrations not allowing the assumption of a specific trend for resulting blend properties, but nevertheless in the case of a lower PS concentration the tensile impact strength exceeded the value of virgin PP. Since PS and PP are widely used, the findings of this work could not only be relevant for the generation of more versatile blends compared to virgin components but also for recycling purposes, allowing the enhancement of specific properties facilitating the production of more valuable secondary materials.

The influence of two peroxides (peroxydicarbonate/dilauroyl peroxide) with various concentrations (10–200 mmol/kg PP) and their effective opportunity to introduce long chain branched (LCB) were investigated. The dependence of a single and double extrusion step and the changes of the properties were studied. Experiments were carried out in a single screw extruder at 180°C for the first extrusion step (modification) and at 240°C for the second extrusion step (processing simulation). Melt flow rate and dynamic rheological properties were studied at a measuring temperature of 230°C. For the definitive determination of long chain branched polypropylene (LCB‐PP) served the extensional rheology measurements. The mechanical properties were examined via tensile test and impact tensile test. Summarized, LCB (melt strength) could be observed via extensional rheology for all modified specimens and the mechanical properties were maintained or even improved for the modified samples. Particularly, samples containing dilauroyl peroxide display excellent mechanical properties in this study.

Blends of two long-chain branched polypropylenes (LCB-PP) and five linear polypropylenes (L-PP) were prepared in a single screw extruder at 240 °C. The two LCB-PPs were self-created via reactive extrusion at 180 °C by using dimyristyl peroxydicarbonate (PODIC C126) and dilauroyl peroxide (LP) as peroxides. For blending two virgin and three recycled PPs like coffee caps, yoghurt cups and buckets with different melt flow rate (MFR) values were used. The influence of using blends was assessed by investigating the rheological (dynamic and extensional rheology) and mechanical properties (tensile test and impact tensile test). The dynamic rheology indicated that the molecular weight as well as the molecular weight distribution could be increased or broadened. Also the melt strength behavior could be improved by using the two peroxide modified LCB-PP blends on the basis of PODIC C126 or PEROXAN LP (dilauroyl peroxide). In addition, the mechanical properties were consistently enhanced or at least kept constant compared to the original material. In particular, the impact tensile strength but also the elongation at break could be increased considerably. This study showed that the blending of LCB-PP can increase the investigated properties and represents a promising option, especially when using recycled PP, which demonstrates a real “up-cycling” process.