The formation of Fe-Zn intermetallic compounds, as relevant in the commercial product galvannealed steel sheet, was investigated by scanning electron microscopy and different methods of X-ray diffraction. A scanning electron microscope with high resolution was applied to investigate the layers of the galvannealed coating and its topography. Grazing incidence X-ray diffraction (GID) was preferred over conventional Bragg-Brentano geometry for analysing thin crystalline layers because of its lower incidence angle alpha and its lower depth of information. Furthermore, in situ experiments at an environmental scanning electron microscope (ESEM) with an internal heating plate and at an X-ray diffractometer equipped with a high-temperature chamber were carried out. Thus, it was possible to investigate the phase evolution during heat treatment by X-ray diffraction and to display the growth of the zeta crystals in the ESEM.

Vysoké učení technické v Brně, Fakulta stavební, Veveří 331/95, 602 00 Brno AbstraktZvýšená schopnost alkalicky aktivovaných pojiv přenášet elektrický náboj se stala atraktivním tématem ve výzkumu věnovaném multifunkčním materiálům se senzorickými, samozahřívacími a dalšími progresivními vlastnostmi. Tato studie je zaměřena na senzorické vlastnosti metakaolinových geopolymerních malt s 0,05 a 0,10 % uhlíkových nanotrubiček při cyklickém zatěžování v tlaku. Zkušební tělesa s vloženými měděnými elektrodami byla podrobena dvěma různým režimům tlakového zatěžování s kontinuálním sledováním napětí a elektrického odporu. Referenční i modifikované geopolymerní malty vykazovaly dobrou odezvu na působící zatížení, přesto byly zaznamenány změny v citlivosti a strukturních deformacích.