SummaryIn this paper the surfaces of butt welded joints in steel tubes were analyzed using an optical 3D measurement system to determine the morphology and topographic parameters. It was established that pollution of the argon shield gas with oxygen did not influence the width of the heat-affected zone. However, the composition of the shield gas significantly influenced the surface asymmetry, Ssk, and its inclination Sku. The measurement of these parameters enabled the selection of a higher quality surface, which was visually proven by the reduction in discoloration of the surface of the weld joint. High quality surfaces eliminate a potential habitat for bacteria and a future source of corrosion as well as providing less resistance to fluid flow.

No abstract

The objective of the investigation was analysis of the wear of milling cutters made of sintered carbide and of boron nitride. The article presents the life period of the cutting edges and describes industrial conditions of the applicability of tools made of the materials under investigation. Tests have been performed on modern toroidal and ball-end mill cutters. The study has been performed within a production facility in the technology of high speed machining of 55NiCrMoV6 and X153CrMoV12 hardened steel. The analysed cutting speed is a parameter which significantly influences the intensity of heat generated in the cutting zone. Due to the wear characteristics, two areas of applicability of the analysed tools have been distinguished. For v c 300 m/min, sintered carbide edges are recommended; for v c . 500 m/min, boron nitride edges. For 300 v c 500 m/min, a transition area has been observed. It has been proved that the application of sintered carbide edges is not economically justified above certain cutting speed.