This work demonstrates the feasibility of superhydrophilic polyelectrolyte brush coatings for anti-icing applications. Five different types of ionic and nonionic polymer brush coatings of 25-100 nm thickness were formed on glass substrates using silane chemistry for surface premodification followed by polymerization via the SI-ATRP route. The cationic [2-(methacryloyloxy)ethyl]trimethylammonium chloride] and the anionic [poly(3-sulfopropyl methacrylate), poly(sodium methacrylate)] polyelectrolyte brushes were further exchanged with H+, Li+, Na+, K+, Ag+, Ca2+, La3+, C16N+, F-, Cl-, BF4-, SO4(2-), and C12SO3- ions. By consecutive measurements of the strength of ice adhesion toward ion-incorporated polymer brushes on glass it was found that Li+ ions reduce ice adhesion by 40% at -18 °C and 70% at -10 °C. Ag+ ions reduce ice adhesion by 80% at -10 °C relative to unmodified glass. In general, superhydrophilic polyelectrolyte brushes exhibit better anti-icing property at -10 °C compared to partially hydrophobic brushes such as poly(methyl methacrylate) and surfactant exchanged polyelectrolyte brushes. The data are interpreted using the concept of a quasi liquid layer (QLL) that is enhanced in the presence of highly hydrated ions at the interface. It is suggested that the ability of ions to coordinate water is directly related to the efficiency of a given anti-icing coating based on the polyelectrolyte brush concept.

This work features the controllability of surface-initiated atom transfer radical polymerization (SI-ATRP) of methyl methacrylate, initiated by a multilayered 2-bromoisobutyryl moiety formed via diazonium chemistry. The thickness as a function of polymerization time has been studied by varying different parameters such as the bromine content of the initiator layer, polarity of reaction medium, ligand type (L), and the ratio of activator (Cu(I)) to deactivator (Cu(II)) in order to ascertain the controllability of the SI-ATRP process. The variation of thickness versus surface concentration of bromine shows a gradual transition from mushroom to brush-type conformation of the surface anchored chains in both polar and nonpolar reaction medium. Interestingly, it is revealed that very thick polymer brushes, on the order of 1 μm, can be obtained at high bromine content of the initiator layer in toluene. The initial polymerization rate and the overall final thickness are higher in the case of nonpolar solvent (toluene) compared to polar medium (acetonitrile or N,N-dimethylformamide). The ligand affects the initial rate of polymerization, which correlates with the redox potentials of the pertinent Cu(II)/Cu(I) complexes (L = Me(6)TREN, PMDETA, and BIPY). It is also observed that the ability of polymer brushes to reinitiate depends on the initial thickness and the solvent used for generating it.

Redox grafting of aryldiazonium salts containing redox units may be used to form exceptionally thick covalently attached conducting films, even in the micrometers range, in a controlled manner on glassy carbon and gold substrates. With the objective to investigate the mechanism of this process in detail, 1-anthraquinone (AQ) redox units were immobilized on these substrates by electroreduction of 9,10-dioxo-9,10-dihydroanthracene-1-diazonium tetrafluoroborate. Electrochemical quartz crystal microbalance was employed to follow the grafting process during a cyclic voltammetric sweep by recording the frequency change. The redox grafting is shown to have two mass gain regions/phases: an irreversible one due to the addition of AQ units to the substrate/film and a reversible one due to the association of cations from the supporting electrolyte with the AQ radical anions formed during the sweeping process. Scanning electrochemical microscopy was used to study the relationship between the conductivity of the film and the charging level of the AQ redox units in the grafted film. For that purpose, approach curves were recorded at a platinum ultramicroelectrode for AQ-containing films on gold and glassy carbon surfaces using the ferro/ferricyanide redox system as redox probe. It is concluded that the film growth has its origin in electron transfer processes occurring through the layer mediated by the redox moieties embedded in the organic film.

 Users may download and print one copy of any publication from the public portal for the purpose of private study or research.  You may not further distribute the material or use it for any profit-making activity or commercial gain  You may freely distribute the URL identifying the publication in the public portal If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.

This study elucidates the influence of the atom transfer radical polymerization initiator structure, monolayer versus disordered multilayer, on the growth kinetics and the structural transition of poly(methyl methacrylate) (PMMA) brush layers. The multilayer initiator film, prepared by acylation of the electrografted 2‐phenylethanol layer using 2‐bromoisobutyryl bromide, consists of ∼4.6 times more tert‐butyl bromide groups compared to monolayer initiator prepared by self assembly technique. The results demonstrate the formation of precursor complex between CuI catalyst and the bromine initiator as a prerequisite step before the onset of polymerization. Furthermore, the PMMA brushes formed by the polymerization from the multilayered initiator layer at 50 °C are 20‐fold thicker compared to the polymerization at 25 °C due to the swelling of the multilayered initiator film. In contrast, the thickness of the PMMA layer on the monolayer initiator is less affected by the polymerization temperature. By varying the initiator density on the surface, the solvent content in the PMMA layer is shown to vary from 15% to 94%, resulting in the transition from concentrated over semidiluted to diluted brushes. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012