Commercially pure (c.p.) titanium grade IV with a bimodal microstructure is a promising material for biomedical implants. The influence of the processing parameters on the physical, microstructural, and mechanical properties was investigated. The bimodal microstructure was achieved from the blends of powder particles with different sizes, while the porous structure was obtained using the space-holder technique (50 vol.% of ammonium bicarbonate). Mechanically milled powders (10 and 20 h) were mixed in 50 wt.% or 75 wt.% with c.p. titanium. Four different mixtures of powders were precompacted via uniaxial cold pressing at 400 MPa. Then, the specimens were sintered at 750 °C via hot pressing in an argon gas atmosphere. The presence of a bimodal microstructure, comprised of small-grain regions separated by coarse-grain ones, was confirmed by optical and scanning electron microscopies. The samples with a bimodal microstructure exhibited an increase in the porosity compared with the commercially available pure Ti. In addition, the hardness was increased while the Young’s modulus was decreased in the specimens with 75 wt.% of the milled powders (20 h).

Titanium (Ti) and its alloys are used for biomedical applications because of their high resistance to corrosion, good strength-to-weight ratio, and high fatigue resistance. However, a problem that compromises the performance of the material is the mismatch between Young’s modulus of Ti and the bone, which brings about stress shielding. One strategy that has been investigated to reduce this difference is the manufacture of Ti-based foams, using powder metallurgy (PM) methods, such as the space-holder technique. However, in the uniaxial compaction, both non-uniform density distribution and mechanical properties remain because of the compaction method. This work studies the influence of compaction by adopting a floating-action die related to a single-action die (SAD), on the density of green and sintered Ti foams with porosities around 50 vol.% characterized by optical microscopy, ultrasound analysis, compression tests, and microhardness. The compaction process employing a floating-action die generates Ti foams with a higher density up to 10% with more control of the spacer particle added compared to the single-action die. Furthermore, compaction method has no relevant effect on microhardness and Young’s modulus, which allows getting better consolidated samples with elastic modules similar to those of human bone.