In the present work, the use of a commercial ionic liquid as a convenient solvent medium for graphite exfoliation in mild and easy conditions without any chemical modification is presented. To confirm the presence of few layer graphene, its dispersion, which exhibits Tyndall effect, was characterized by Raman and UV spectroscopies, and atomic force and field emission electron microscopies. It is noteworthy that, by gravimetric analysis, a graphene concentration as high as 5.33 mg ml À1 was determined, which is the highest value reported so far in any solvent.

Frontal polymerization has been successfully used to synthesize poly(N-isopropylacrylamide) nanocomposite hydrogels containing graphene. The latter was directly achieved by ultrasound treatment of a dispersion of graphite in N-methylpyrrolidone. The dispersion, having the concentration of 2.21 g L À1 , was characterized by TEM analysis and mixed with suitable amounts of N-isopropylacrylamide for the synthesis of graphene-containing nanocomposite polymer hydrogels. The nanocomposite hydrogels were analyzed by SEM and Raman spectroscopy, and their swelling and rheological properties were investigated. It was found that graphene strongly influences the swelling ratio, dramatically increasing it, even if present in small amounts. Finally, the rheological properties of the hydrogels were correlated with the graphene content: G 0 modulus and complex viscosity were found to increase with increasing nanofiller concentration, thus indicating the occurrence of good interactions between the two phases. Nevertheless, at a high concentration (i.e., 0.13 wt.%), graphene showed a lubrication effect, lowering the rheological parameters and approaching the same pseudoplastic behaviour of the unfilled material.

Frontal polymerization was used as an alternative technique for the preparation of super water absorbent hydrogels obtained from acrylamide and 3‐sulfopropyl acrylate, potassium salt (SPAK) in the presence of N,N′‐methylene‐bisacrylamide as a crosslinker. All samples were synthesized in dimethyl sulfoxide, and their swelling behavior in water was investigated. It was found that their features are dependent on the monomer ratio used, which influenced the porous morphology, and consequently, the swelling capability. The swelling ratio ranges from about 1000% for the acrylamide homopolymer up to 14,000% for the sample containing 87.5 mol % of SPAK, thus indicating that this parameter can be easily tuned by using the appropriate monomer ratio. The affinity towards water was eventually confirmed by contact angle analysis. Polymer hydrogels made from at least 62.5 mol % SPAK exhibit a thermoresponsive behavior, with a lower critical solution temperature of ∼30 °C. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2486–2490, 2010