To study the physical and chemical properties of grout containing fly ash, Class II fly ash was used as a mineral admixture and mixed with silicate cement to produce grout, and the rheological properties, strength properties, hydration properties, and microscopic mechanism were studied. The results of the study showed the following. The incorporation of fly ash reduced the thixotropic area of the composite cement slurry, which facilitated pumping in the pipeline conveying process. The inclusion of fly ash reduced the yield stress and plastic viscosity of the cement paste, but the rheological index increased and then decreased with the increase in fly ash, and the composite paste had the lowest degree of shear thinning at 30% fly ash inclusion. The incorporation of fly ash reduced the hydration exothermic rate and total hydration exothermic amount of the composite slurry and prolonged the hydration induction period, but the promotion effect of fly ash on the hydration rate of cement was obvious at 10% fly ash admixture. The admixture of fly ash increased the empty volume of the composite slurry, but the effect on the most probable aperture was not significant, and the porosity of the system increased, resulting in a decrease in compressive strength. The effect of adding fly ash on the hydration products was reflected mainly by the C-S-H gel produced by cement hydration and the change in calcium alumina and Ca(OH)2. Fly ash does not directly participate in the hydration reaction of cement, but it can promote cement hydration and increase the reaction rate of cement. By analyzing the rheological properties, mechanical properties, and hydration properties of fly ash composite cement paste, the comprehensive analysis found that the rheological properties are excellent when the fly ash admixture is 20–30%, and the water–cement ratio can be reduced to improve the strength without affecting the pumping demand.

No abstract

The properties of blended cement containing 0%, 20%, and 50% iron tailing powder (ITP) at 20 °C and 60 °C were investigated by determining the hydration heat, microstructure, and compressive strength. The addition of ITP decreases the exothermic rate and cumulative hydration heat of blended cement at 20 °C. The high temperature increases the hydration rate and leads to the hydration heat of blended cement containing 20% ITP higher than that of Portland cement. Increasing the amount of ITP decreases the non-evaporable water content and Ca(OH)2 content as well as compressive strength at both of the two studied temperatures. The addition of ITP coarsens the early-age pore structure but improves the later-age pore structure at 20 °C. The high temperature significantly improves the early-age properties of blended cement containing ITP, but it is detrimental to the later-age properties development. The reaction of ITP is limited even at high temperature. The large ITP particles bond poorly with surrounding hydration products under early high-temperature curing condition. The properties of blended cement containing a large amount of ITP are much poorer at high temperature.