Carbon nanomaterials have been shown to rapidly evolve heat in response to electromagnetic fields. Initial studies focused on the use of microwaves, but more recently, it was discovered that carbon...

No abstract

Composites of nanocarbon network structures are interesting materials, combining mechanical properties and electrical conductivity superior to those of granular systems. Hence, they are envisaged to have applications as electrodes for energy storage and transfer. Here, we show a new processing route using Joule heating for a nanostructured network composite of carbon nanotube (CNT) fabrics and an inorganic phase (namely, MoS 2 ), and then study the resulting structure and properties. To this end, first, a unidirectional fabric of conductive CNT bundles is electrochemically coated with MoS 2 . Afterward, the conformally coated inorganic phase is crystallized via heat generated by direct current passing through the CNT ensemble. The Joule heating process is rapid (maximum heating rate up to 31.7 °C/s), enables accurate temperature control, and takes only a few minutes. The resulting composite material combines a high electrical conductivity of up to 1.72 (±0.25) × 10 5 S/m, tensile modulus as high as 8.82 ± 5.5 GPa/SG, and an axial tensile strength up to 200 ± 58 MPa/SG. Both electrical and mechanical properties are orders of magnitude above those of wet-processed nanocomposites of similar composition. The extraordinary longitudinal properties stem from the network of interconnected and highly aligned CNT bundles. Conductivity and modulus follow approximately a rule of mixtures, similar to a continuous fiber composite, whereas strength scales almost quadratically with the mass fraction of the inorganic phase due to the inorganic constraining realignment of CNTs upon stretching. This processing route is applicable to a wide range of nanocarbon-based composites with inorganic phases, leading to composites with specific strength above steel and electrical conductivity beyond the threshold for electronic limitations in battery electrodes.

This study demonstrates a new and sustainable methodology for recycling continuous carbon fibers from end-of-life thermoset composite parts using Joule heating. This process addresses the longstanding challenge of efficiently recovering carbon fibers from composite scrap and reusing them to make fresh composites. The conductive carbon fibers volumetrically heat up when an electric current is passed through them, which in turn rapidly heats up the surrounding matrix sufficiently to degrade it. Fibers can be easily separated from the degraded matrix after the direct current (DC) heating process. Fibers reclaimed using this method were characterized to determine their tensile properties and surface chemistry, and compared against both as-received fibers and fibers recycled using conventional oven pyrolysis. The DC-and oven-recycled fibers yielded similar elastic modulus when compared against asreceived fibers; however, an around 10-15 % drop was observed in the tensile strength of fibers recycled using either method. Surface characterization showed that DC-recycled fibers and asreceived fibers had similar types of functional groups. To demonstrate the reusability of recycled fibers, composites were fabricated by impregnation with epoxy resin and curing. The mechanical properties of these recycled carbon fiber composites (rCFRCs) were compared against conventional recycling methods, and similar modulus and tensile strength values were obtained. This study establishes DC heating as a scalable out-ofoven approach for recycling carbon fibers.