Ultrahigh density arrays of conducting polypyrrole (PPy) nanorods are fabricated directly on the indium-tin oxide coated glass by an electropolymerization within a porous diblock copolymer template. The nanorods are shown to have conductivity much higher than thin PPy films, due to the high degree of chain orientation, even though the separation distance for two neighboring PPy main chains is as small as 0.37 nm. The ultrahigh density arrays of conducting polymer nanorods have potential applications as sensor materials, nanoactuators, and organic photovoltaic devices.

Electrically programmable fuse‐type polymer memory devices based on hyperbranched copper phthalocyanine polymer thin films are fabricated. The devices have novel write‐once‐read‐many (WORM) memory characteristics, with a high ON/OFF current ratio (of 106) and a high electrical stability, thus opening up the possibility of a low‐cost mass production of high‐performance, nonvolatile polymer memory devices.

Electrical properties of contacts formed between conducting polymers and noble metal nanoparticles have been examined using current-sensing atomic force microscopy (CS-AFM). Contacts formed between electrochemically prepared pi-conjugated polymer films such as polypyrrole (PPy), poly(3-methylthiophene) (P3MeT), as well as poly(3,4-ethylenedioxythiophene) (PEDOT) and noble metal nanoparticles including platinum (Pt), gold (Au), and silver (Ag) have been examined. The Pt nanoparticles were electrochemically deposited on a pre-coated PPy film surface by reducing a platinum precursor (PtCl62-) at a constant potential. Both current and scanning electron microscopic images of the film showed the presence of Pt islands. The Au and Ag nanoparticles were dispersed on the P3MeT and PEDOT film surfaces simply by dipping the polymer films into colloid solutions containing Au or Ag particles for specified periods (5 to approximately 10 min). The deposition of Au or Ag particles resulted from either their physical adsorption or chemical bonding between particles and the polymer surface depending on the polymer. When compared with PPy, P3MeT and PEDOT showed a stronger binding to Au or Ag nanoparticles when dipped in their colloidal solutions for the same period. This indicates that Au and Ag particles are predominantly linked with the sulfur atoms via chemical bonding. Of the two, PEDOT was more conductive at the sites where the particles are connected to the polymer. It appears that PEDOT has better aligned sulfur atoms on the surface and is strongly bonded to Au and Ag nanoparticles due to their strong affinity to gold and silver. The current-voltage curves obtained at the metal islands demonstrate that the contacts between these metal islands and polymers are ohmic.