Seven titanium complexes bearing fluorine-containing phenoxy-imine chelate ligands, TiCl(2)[eta(2)-1-[C(H)=NR]-2-O-3-(t)Bu-C(6)H(3)](2) [R = 2,3,4,5,6-pentafluorophenyl (1), R = 2,4,6-trifluorophenyl (2), R = 2,6-difluorophenyl (3), R = 2-fluorophenyl (4), R = 3,4,5-trifluorophenyl (5), R = 3,5-difluorophenyl (6), R = 4-fluorophenyl (7)], were synthesized from the lithium salt of the requisite ligand and TiCl(4) in good yields (22%-76%). X-ray analysis revealed that the complexes 1 and 3 adopt a distorted octahedral structure in which the two phenoxy oxygens are situated in the trans-position while the two imine nitrogens and the two chlorine atoms are located cis to one another, the same spatial disposition as that for the corresponding nonfluorinated complex. Although the Ti-O, Ti-N, and Ti-Cl bond distances for complexes 1 and 3 are very similar to those for the nonfluorinated complex, the bond angles between the ligands (e.g., O-Ti-O, N-Ti-N, and Cl-Ti-Cl) and the Ti-N-C-C torsion angles involving the phenyl on the imine nitrogen are different from those for the nonfluorinated complex, as a result of the introduction of fluorine atoms. Complex 1/methylalumoxane (MAO) catalyst system promoted living ethylene polymerization to produce high molecular weight polyethylenes (M(n) > 400 000) with extremely narrow polydispersities (M(w)/M(n) < 1.20). Very high activities (TOF > 20 000 min(-1) atm(-1)) were observed that are comparable to those of Cp(2)ZrCl(2)/MAO at high polymerization temperatures (25, 50 degrees C). Complexes 2-4, which have a fluorine atom adjacent to the imine nitrogen, behaved as living ethylene polymerization catalysts at 50 degrees C, whereas complexes 5-7, possessing no fluorine adjacent to the imine nitrogen, produced polyethylenes having M(w)/M(n) values of ca. 2 with beta-hydrogen transfer as the main termination pathway. These results together with DFT calculations suggested that the presence of a fluorine atom adjacent to the imine nitrogen is a requirement for the high-temperature living polymerization, and the fluorine of the active species for ethylene polymerization interacts with a beta-hydrogen of a polymer chain, resulting in the prevention of beta-hydrogen transfer. This catalyst system was used for the synthesis of a number of unique block copolymers such as polyethylene-b-poly(ethylene-co-propylene) diblock copolymer and polyethylene-b-poly(ethylene-co-propylene)-b-syndiotactic polypropylene triblock copolymer from ethylene and propylene.

No abstract

No abstract

The control of hydroxylated polyethylene (PE) structures was investigated in the copolymerization of ethylene with allyl alcohol or 10‐undecen‐1‐ol with a specific metallocene, methylaluminoxane, and trialkyl aluminum catalyst system through changes in the copolymerization conditions. The incorporation of allyl alcohol into the PE backbones was controllable through changes in the trialkyl aluminum, leading to terminally hydroxylated PE or a copolymer possessing hydroxyalkyl side chains. The copolymerization of ethylene with 10‐undecen‐1‐ol gave copolymers with hydroxyalkyl side chains of various contents with a variety of molecular weights through changes in the copolymerization conditions. The obtained copolymers were useful as macroinitiators that allowed polar polymer segments to grow on the PE backbones, leading to the creation of graft copolymers that possessed PE and polar polymer segments. In this way, polyethylene‐g‐poly(propylene glycol) (PE‐g‐PPG) and polyethylene‐g‐poly(ϵ‐caprolactone) (PE‐g‐PCL) were synthesized. The 13C NMR analysis of PE‐g‐PPG suggested that all the hydroxyl groups were consumed for propylene oxide polymerization, and transmission electron microscopy demonstrated nanoorder phase separation and indistinct phase boundaries. 13C NMR and gel permeation chromatography analyses indicated the formation of PE‐g‐PCL, in which 36–80 mol % of the hydroxyl groups worked as initiators for ϵ‐caprolactone polymerization. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3657–3666, 2003

Polyethylene‐block‐poly(methyl methacrylate) (PE‐b‐PMMA) was successfully synthesized through the combination of metallocene catalysis with living radical polymerization. Terminally hydroxylated polyethylene, prepared by ethylene/allyl alcohol copolymerization with a specific zirconium metallocene/methylaluminoxane/triethylaluminum catalyst system, was treated with 2‐bromoisobutyryl bromide to produce terminally esterified polyethylene (PE‐Br). With the resulting PE‐Br as an initiator for transition‐metal‐mediated living radical polymerization, methyl methacrylate polymerization was subsequently performed with CuBr or RuCl2(PPh3)3 as a catalyst. Then, PE‐b‐PMMA block copolymers of different poly(methyl methacrylate) (PMMA) contents were prepared. Transmission electron microscopy of the obtained block copolymers revealed unique morphological features that depended on the content of the PMMA segment. The block copolymer possessing 75 wt % PMMA contained 50–100‐nm spherical polyethylene lamellae uniformly dispersed in the PMMA matrix. Moreover, the PE‐b‐PMMA block copolymers effectively compatibilized homopolyethylene and homo‐PMMA at a nanometer level. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3965–3973, 2003