CoC(x) nanoparticles encapsulated in carbon shells were synthesized using a pulsed plasma in liquid ethanol. This is the first time that monolithic cubic phase cobalt carbide nanoparticles have been obtained. X-ray diffraction refinement of the nanoparticles showed that the lattice parameter of prepared cubic phase cobalt carbide is larger than that of CoC(x) (44-0962) and cubic phase Co (15-0806 and 01-1259). The x-ray absorption fine structure spectra near the Co K-edge of the synthesized sample indicated differences from commercial metallic cobalt and cobalt oxide samples. High resolution transmission electron microscopy revealed that a thin carbon coating covered the surface of the nanoparticles. These carbon layers might isolate core CoC(x) material from the outside environment, and allow functionalization by carboxyl groups for the further purpose of targeted drug delivery. The obtained CoC(x)@C particles, with a crystallite size of about 10 nm confirmed by the electron microscope, aggregate into 20-40 nm secondary particles in distilled water as shown by dynamic light scattering, and possess high saturation magnetization of about 120 emu g(-1). The sodium 3'-[1-(phenylaminocarbonyl)-3,4-tetrazolium]-bis(4-methoxy-6-nitro)benzene sulfonic acid hydrate assay and defragmentation of deoxyribonucleic acid on MCF-7 cells after incubation with particles indicate relatively low cytotoxicity of CoC(x)@C nanoparticles, compared with micro-sized and nano-sized metallic cobalt particles and commonly used iron oxides. For the small sized CoC(x)@C particles, the release of cobalt ions was checked by a chelation method with ethylenediaminetetraacetic acid solution to be at a very low level compared with other reference materials.

No abstract

High temperature stable WC 12x @C and TiC@C coreshell nanoparticles by pulsed plasma in liquid3

No abstract

The synthesis of wurtzite-type ZnS nanoparticles by an electric discharge submerged in molten sulfur is reported. Using a pulsed plasma between two zinc electrodes of diameter 5 mm in molten sulfur, we have synthesized high-temperature phase (wurtzite-type) ZnS nanocrystals with an average size of about 20 nm. The refined lattice parameters of the synthesized wurtzite-type ZnS nanoparticles were found to be larger than those of the reported ZnS (JCPDS card no 36-1450). Synthesis of ZnMgS (solid solution of ZnS and MgS) was achieved by using ZnMg alloys as both cathode and anode electrodes. UV-visible absorption spectroscopy analysis showed that the absorption peak of the as-prepared ZnS sample (319 nm) displays a blue-shift compared to the bulk ZnS (335 nm). Photoluminescence spectra of the samples revealed peaks at 340, 397, 423, 455 and 471 nm, which were related to excitonic emission and stoichiometric defects.