cathodoluminescence (STRCL) spectroscopy is implemented to assess the local carrier dynamics in a 70-nm-thick, very low threading dislocation (TD) density, pseudomorphic m-plane In 0:05 Ga 0:95 N epilayer grown on a freestanding GaN substrate by metalorganic vapor phase epitaxy. Although TDs or stacking faults are absent, sub-micrometer-wide zonary patterns parallel to the c-axis and 2-m-long-axis figureof-8 patterns parallel to the a-axis are clearly visualized in the monochromatic cathodoluminescence intensity images. Because the STRCL measurement reveals very little spatial variation of low-temperature radiative lifetime, the considerable peak energy variation is interpreted to originate from nonidentical In-incorporation efficiency for the growing surfaces exhibiting various miscut angles. The figure-of-8 patterns are ascribed to originate from the anisotropic, severe m-plane tilt mosaic along the a-axis of the GaN substrate, and the zonary patterns may originate from the m-plane tilt mosaic along the c-axis. #
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.