We have proposed a new extrusion process functionally combined with torsion. Extrusion-torsion simultaneous processing is a very attractive technique for fabricating a rod-shape material with high strength and excellent workability. To improve the hardness, the aging treatment was performed with AZ91D magnesium alloy screw thread-rolled at room temperature using extrusion-torsion simultaneous processing. The distribution of hardness from the tip to center in as thread-rolled screw was modified to uniform distribution by the isothermal aging treatment at 423 K for 460.8 ks. The peak hardness was not depended on the working temperature and rotation speed during extrusion-torsion simultaneous processing. β-Mg17Al12 precipitates are obviously grown in as peak-aged condition comparing with as thread-rolled condition.

Extrusion-torsion simultaneous processing is a very attractive technique for fabricating a rod-shape material with fine grain and random texture. We have proposed a new screw form rolling process combined with preliminary extrusion-torsion simultaneous working. Microstructure evolution and mechanical property change of AZ91D magnesium alloy during extrusion-torsion simultaneous processing was examined through microstructure observation, X-ray diffraction analysis and micro-Vickers hardness measurement. By the addition of torsion, the crystal orientation of AZ91D magnesium alloy workpiece was drastically changed from basal crystalline orientation to the random orientation. Crystal grain occurred through the dynamic recrystallization and tended to coarsen with an increase of extrusion-torsion temperature. Grain refinement under 2 um was achieved at the lowest extrusion-torsion temperature of 523 K. M8 gauge AZ91D magnesium alloy screw was successfully formed at room temperature using the extrusion-twisted workpiece preliminary solution treating at 678 K for 345.6 ks. It was found that the extrusion-torsion temperature of 678 K must be selected to fabricate the good screw without any defects.