Wood heat treatment is an attractive alternative to improve decay resistance of wood species with low natural durability. However, this improvement of durability is realized at the expense of the mechanical resistance. Decay resistance and mechanical properties are strongly correlated to thermal degradation of wood cells wall components. Mass loss resulting from this degradation is a good indicator of treatment intensity and final treated wood properties. However, the introduction of a fast and accurate system for measuring this mass loss on an industrial scale is very difficult. Nowadays, many studies are conducted on the determination of control parameters which could be correlated with the treatment conditions and final heat treated wood quality such as decay resistance. The aim of this study is to investigate the relations between kinetics of temperature used during thermal treatment process representing heat treatment intensity, mass losses due to thermal degradation and conferred properties to heat treated wood. It might appear that relative area of treatment temperature curves is a good indicator of treatment intensity. Heat treatment with different treatment conditions (temperature-time) have been performed under vacuum, on four wood species (one hardwood and three softwoods) in order to obtain thermal degradation mass loses of 8, 10 and 12%. For each experiment, relative areas corresponding to temperature kinetics, mass loss, decay resistance and mechanical properties have been determined. Results highlight the statement that the temperature curves' area constitutes a good indicator in the prediction of needed treatment intensity, to obtain required wood durability and mechanical properties such as bending resistance and Brinell hardness.

Thermal modification processes have been developed to increase the biological durability and dimensional stability of wood. The aim of this paper was to study the influence of ThermoWood Ò treatment intensity on improvement of wood decay resistance against soil-inhabiting microorganisms , brown/white rots and termite exposures. All of the tests were carried out in the laboratory with two different complementary research materials. The main research material consisted of ash (Fraxinus excelsior L.) wood thermally modified at temperatures of 170, 200, 215 and 228°C. The reference materials were untreated ash and beech wood for decay resistance tests, untreated ash wood for soil bed tests and untreated ash, beech and pine wood for termite resistance tests. An agar block test was used to determine the resistance to two brown-rot and two white-rot fungi according to CEN/TS 15083-1 directives. Durability against soil-inhabiting microorganisms was determined following the CEN/TS 15083-2 directives, by measuring the weight loss, modulus of elasticity (MOE) and modulus of rupture (MOR) after incubation periods of 24, 32 and 90 weeks. Finally, Reticulitermes santonensis species was used for determining the termite attack resistance by non-choice screening tests, with a size sample adjustment according to EN 117 standard directives on control samples and on samples which have previously been exposed to soil bed test. Thermal modification increased the biological durability of all samples. However, high thermal modification temperature above 215°C, represented by a wood mass loss (ML%) due to thermal degradation of 20%, was needed to reach resistance against decay comparable with the durability classes of ''durable'' or ''very durable'' in the soil bed test. The brown-rot and white-rot tests gave slightly better durability classes than the soil bed test. Whatever the heat treatment conditions are, thermally modified ash wood was not efficient against termite attack neither before nor after soft rot degradation.