Suspension plasma-sprayed coatings are produced using fine-grained feedstock. This allows to control the porosity and to achieve low thermal conductivity which makes the coatings attractive as topcoats in thermal barrier coatings (TBCs). Used in gas turbine applications, TBCs are exposed to high temperature exhaust gases which lead to microstructure alterations. In order to obtain coatings with optimized thermomechanical properties, microstructure alterations like closing of pores and opening of cracks have to be taken into account. Hence, in this study, TBC topcoats consisting of 4 mol.% yttria-stabilized zirconia were heat-treated in air at 1150°C and thereafter the coating porosity was investigated using image analysis (IA) and nuclear magnetic resonance (NMR) cryoporometry. Both IA and NMR cryoporometry showed that the porosity changed as a result of the heat treatment for all investigated coatings. In fact, both techniques showed that the fine porosity decreased as a result of the heat treatment, while IA also showed an increase in the coarse porosity. When studying the coatings using scanning electron microscopy, it was noticed that finer pores and cracks disappeared and larger pores grew slightly and achieved a more distinct shape as the material seemed to become more compact.

Polarised Raman spectroscopy is used to reveal the orientation of specific T–O–T bonds in singe crystals of ZSM-5 and silicalite-1.

The isomorphous substitution of Si with metals other than Al in zeotype frameworks allows for tuning the acidity of the zeotype and, therefore, to tailor the catalyst’s properties as a function of the desired catalytic reaction. In this study, B, Ga, and Ti are incorporated in the MFI framework of silicalite samples and the following series of increasing acidity is observed: Ti-silicalite < B-silicalite < Ga-silicalite. It is also observed that the lower the acidity of the sample, the easier the methanol desorption from the zeotype surface. In the target reaction, namely the direct conversion of methane to methanol, methanol extraction is affected by the zeotype acidity. Therefore, the results shown in this study contribute to a more enriched knowledge of this reaction.

A large variety of coatings are used to protect structural engineering materials from corrosion, wear, and erosion, and to provide thermal insulation. In this work, yttria-stabilized zirconia coatings produced by suspension plasma spraying were investigated with respect to their microstructure and especially their porosity, as the porosity affects the thermal insulation of the underlying component. To determine porosity, pore size distribution, and pore shape, the coatings were investigated using novel advanced characterization techniques like NMR cryoporometry and X-ray microscopy. In general, the porosity is inhomogeneously distributed and the coatings showed a large variety of pore sizes ranging from a few nanometers to micrometers.