Among all recognized severe plastic deformation techniques, a new method, called the equal channel forward extrusion process, has been experimentally studied. It has been shown that this method has similar characteristics to other severe plastic deformation methods, and the potential of this new method was examined on the mechanical properties of commercial pure aluminum. The results indicate that approximate 121%, 56%, and 84% enhancements, at the yield strength, ultimate tensile strength, and Vickers micro-hardness measurement are, respectively, achieved after the fourth pass, in comparison with the annealed condition. The results of drop weight impact test showed that the increment of 26% at the impact force, and also decreases of 32%, 15%, and 4% at the deflection, impulse, and absorbed energy, are respectively attained for the fourth pass when compared to the annealed condition. Furthermore, the electron backscatter diffraction examination revealed that the average grain size of the final pass is about 480 nm.

The newly invented cross-flow WESP exhibit particulate collection efficiency of well above 80% when introduced in particulate-laden exhaust flow. This value was obtained using a two cells and three discharge electrodes configuration. The electric field strength has a substantial effect on the collection efficiency. Also, the pressure drop test results indicate that there is a potential to increase the collection area, which, in turn, will increase the collection efficiency further.

No abstract

No abstract

No abstract