The extraction of lanthanum (La) and cerium (Ce) from a bastnasite ore by direct acidic leaching was investigated. The effects of acid concentration and leaching temperature on the extraction of La and Ce from the ore were tested. Using nitric (NHO 3 ), more than 85% of the La and Ce were simultaneously extracted into leach solution whereas the La and Ce dissolutions were determined as less than 85% by using sulfuric acid (H 2 SO 4 ). The La dissolution exceeded 90% by using hydrochloric acid (HCl); however, the Ce dissolution remained below 85% under the following conditions: solid-to-liquid ratio of 20% (w/v), the acid concentration of 20%, leaching temperature of 25 °C and leaching time of 1 h. The result revealed that HNO 3 could be used as a solvent for the maximum simultaneous extraction of the La and Ce from the bastnasite ore. The leaching temperature had no crucial effect on the dissolution of La and Ce when HNO 3 or HCl solutions were preferred as a solvating agent. However, the leaching temperature had a slight positive effect on the dissolutions of La and Ce when H 2 SO 4 was used as a solvent. ÖZDirekt asit liçi ile bir bastnazit cevherinden lantanyum (La) ve seryum (Ce) ekstraksiyonu araştırılmıştır. Bastnazit cevherinden La ve Ce ekstraksiyonuna asit konsantrasyonu ve liç sıcaklığının etkileri test edilmiştir. Nitrik asit (NHO 3 ) kullanarak La ve Ce'un %85'ten fazlası liç çözeltisine alınmıştır ancak çözünme değerleri sülfürik asit (H 2 SO 4 ) kullanıldığında %85'ten az olarak belirlenmiştir. La çözünümü hidroklorik asit (HCl) kullanımıyla %90'ı geçmiştir fakat Ce çözünümü %20 (g/L) katı-sıvı oranı, %20 asit konsantrasyonu, 25 °C liç sıcaklığı ve 1 saat liç süresi şartları altında %85'in altında kalmıştır. Sonuçlar bastnazit cevherinden eş zamanlı olarak maksimum La ve Ce çözünümüne ulaşılabilmek için çözücü olarak HNO3 kullanılabileceğini ortaya koymuştur. Çözücü olarak HNO 3 ve HCl tercih edildiğinde liç sıcaklığının La ve Ce çözünümüne önemli bir etki yapmadığı belirlenmiştir. Fakat çözücü olarak H 2 SO 4 kullanılmasıyla liç sıcaklığının La ve Ce çözünmeleri üzerine hafif bir pozitif etkisi saptanmıştır.

In this study, Faujasite (Na-LSX) (3.5(Ca 0.3 )3.5(Na 0.6 )3.5(Mg 0.1 )Al 7 Si 17 O 48 •32(H 2 O)) type zeolites and Ca-Filipsite (CaK 0.6 Na 0.4 Si 5.2 Al 2.8 O 16 •6(H 2 O)) type zeolites were produced from Sugözü Thermal Power Plant and Çatalağzı Thermal Power Plant fly ashes by alkali fusion method followed by water leaching, respectively. In these methods, fly ashes and sodium hydroxide (NaOH) were mixed in certain proportions and sintered at 600 °C in ash furnace. Then, zeolites were obtained from the ground materials after water leaching and solid/liquid separation, respectively. Cation Exchange Capacity (CEC), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier-Transform Infrared Spectroscopy (FTIR), X-Ray Fluorescence (XRF) and Atomic Absorption Spectrometer (AAS) analyses were used to characterize the synthesized zeolites. The zeolites synthesized with Sugözü fly ashes in a ratio of 1:2 had 136.93 meq/100 g CEC, whereas the CEC of synthesized zeolite from Çatalağzı fly ashes was found to be 247.88 meq/100 g. As a result, zeolites, which can be used as wastewater treatment agent, energy storage material, catalyst and separator, were synthesized by using 2 different Class F fly ash. ÖZBu çalışmada, Sugözü termik santrali uçucu küllerinden sonrasında su liçi ile desteklenen bazik füzyon tekniği kullanılarak fojasit (Na-LSX) (3.5(Ca 0.3 )3.5(Na 0.6 )3.5(Mg 0.1 )Al 7 Si 17 O 48 •32(H 2 O)) türü, Çatalağzı uçucu küllerinden ise aynı tekniği kullanarak Ca-Filipsit (CaK 0.6 Na 0.4 Si 5.2 Al 2.8 O 16 •6(H 2 O))türü zeolitler sentezlenmiştir. Bu yöntemlerde öncelikle yüksek sıcaklıkta kül fırınında uçucu küller ve sodyum hidroksit (NaOH) belirli oranlarda karıştırılarak 600 °C'de sinterlenmiş sonrasında öğütülen malzemelerden saf suda liç işlemi ile zeolitler elde edilmiştir. Katyon Değiştirme Kapasitesi (KDK), X-Işını Kırınımı (XRD), Taramalı Elektron Mikroskobu (SEM), Fourier Dönüşümlü Kızılötesi Spektroskopisi (FTIR), X-Işını Fluoresans (XRF) ve Atomik Adsorpsiyon Spektrometresi (AAS) analizleri ile sentezlenen zeolitler karakterize edilmiştir. Sugözü uçucu külleri ile (1:2 oranda) sentezlenen zeolitler 136,93 meq/100 g KDK'ne sahipken aynı oranda Çatalağzı uçucu külleri ile sentezlenen zeolitlerin 247,88 meq/100 g KDK'ne sahip oldukları belirlenmiştir. Sonuç olarak F sınıfı 2 ayrı uçucu kül kullanarak atıksu arıtıcı, enerji depolayıcı, katalist ve separator olarak kullanılabilecek zeolitler sentezlenmiştir.

No abstract