The organo-clays (OCs) were prepared by a cation exchange reaction between surfactant (cetyltrimethylammonium, C16TMA) from different counterions (Bromide, Chloride, and Hydroxide). The effect of the counterions was investigated on the physico-chemical properties of the prepared organo-clays. The highest uptake of organic cations (1.60 mmol/g) was achieved using cetyl trimethylammonium bromide solution and the lowest value (0.93 mmol/g) was obtained after modification with cetyl trimethylammonium hydroxide solution starting from the same initial ratio of mmol/g of clay greater than 2.40. The arrangement of C16TMA cations within the interlayer space was assumed to be perpendicular with a tilt angle of 32° to the plane of clay sheets instead of being parallel to the clay surface using C16TMAOH solution at the same ratio. Different techniques were used to characterize these materials. The thermal stability of these organ-clays was investigated using an in-situ X-ray diffraction (XRD) technique. The decomposition of the surfactant moiety occurred at temperatures higher than 215 °C and was accompanied with a shrinkage of the basal spacing value to 1.42 nm. These materials were applied in the removal of an acid dye “eosin.” The removed amount of eosin depended on the initial concentrations and the content of surfactants in the organo-clays. The removal of eosin was found to be an endothermic process. The maximum amount of 90 mg/g was achieved. The preheated treatment temperature of two selected OCs did affect the removal properties of eosin. A progressive reduction was observed at temperatures higher than 200 °C. The regeneration of spent OCs was studied and acceptable removal efficiency was maintained after 4 to 6 cycles depending on the used initial concentrations.
Monoclinic bismuth oxide ␣-Bi 2 O 3 nanoparticles were synthesized starting from a mixture of oxalate complexes of bismuth Bi(C 2 O 4 )OH and Bi 2 (C 2 O 4 ) 3 ·xH 2 O obtained by a direct solid-state reaction between a nitrate salt of bismuth and oxalic acid. The starting oxalate mixture precursors were studied by thermal gravimetric analysis (TGA) and characterized by Fourier transform infrared spectroscopy (FTIR). After heat treatment of the oxalate precursors, the obtained oxide ␣-Bi 2 O 3 was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). These ␣-Bi 2 O 3 nanoparticles show low efficiency in photodegradation under UV light irradiation of the dye rhodamine B.
Nano Molybdenum trioxide (α-MoO3) was synthesized in an easy and efficient approach. The removal of methylene blue (MB) in aqueous solutions was studied using this material. The effects of various experimental parameters, for example contact time, pH, temperature and initial MB concentration on removal capacity were explored. The removal of MB was significantly affected by pH and temperature and higher values resulted in increase of removal capacity of MB. The removal efficiency of Methylene blue was 100% at pH = 11 for initial dye concentrations lower than 150 ppm, with a maximum removal capacity of 152 mg/g of MB as gathered from Langmuir model. By comparing the kinetic models (pseudo first-order, pseudo second-order and intraparticle diffusion model) at various conditions, it has been found that the pseudo second-order kinetic model correlates with the experimental data well. The thermodynamic study indicated that the removal was endothermic, spontaneous and favorable. The thermal regeneration studies indicated that the removal efficiency (99%) was maintained after four cycles of use. Fourier Transform Infrared (FTIR) and Scanning Electron Microscopy (SEM) confirmed the presence of the MB dye on the α-MoO3 nanoparticles after adsorption and regeneration. The α-MoO3 nanosorbent showed excellent removal efficiency before and after regeneration, suggesting that it can be used as a promising adsorbent for removing Methylene blue dye from wastewater.
Zinc molybdate (ZnMoO4) was prepared by thermal decomposition of an oxalate complex under a controlled temperature of 500 °C. Analyses of the oxalate complex were carried out using Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). On the other hand, analyses of the synthesized zinc molybdate were carried out by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Brunauer-Emmett-Teller technique (BET). The efficiency of the synthesized catalyst was tested with the reduction reaction of 3-nitrophenol (3-NP), and was also applied as a sorbent for methylene blue dye (MB) in aqueous solutions. The catalytic test of zinc molybdate shows a very high activity. The concentration reduction progress and adsorption of the dye were followed by an ultraviolet-visible (UV-vis) spectrophotometer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.