Electrically conducting fibers and yarns are critical components of future wearable electronic textile (e-textile) devices such as sensors, antennae, information processors, and energy harvesters. To achieve reliable wearable devices, the development of robust yarns with a high conductivity and excellent washability is urgently needed. In the present study, highly conductive and machine-washable silk yarns were developed utilizing a Ag nanowire and PEDOT:PSS composite coating. Ag nanowires were coated on the silk yarn via a dip-coating process followed by coating with the conjugated polymer:polyelectrolyte complex PEDOT:PSS. The PEDOT:PSS covered the Ag nanowire layers while electrostatically binding to the silk, which significantly improved the robustness of the yarn as compared with the Ag nanowire-coated reference yarns. The fabricated conductive silk yarns had an excellent bulk conductivity of up to ∼320 S/cm, which is largely retained even after several cycles of machine washing. To demonstrate that these yarns can be incorporated into e-textiles, the conductive yarns were used to construct an all-textile out-ofplane thermoelectric device and a Joule heating element in a woven heating fabric.

To realize thermoelectric textiles that can convert body heat to electricity, fibers with excellent mechanical and thermoelectric properties are needed. Although poly(3,4‐ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) is among the most promising organic thermoelectric materials, reports that explore its use for thermoelectric fibers are all but absent. Herein, the mechanical and thermoelectric properties of wet‐spun PEDOT:PSS fibers are reported, and their use in energy‐harvesting textiles is discussed. Wet‐spinning into sulfuric acid results in water‐stable semicrystalline fibers with a Young's modulus of up to 1.9 GPa, an electrical conductivity of 830 S cm−1, and a thermoelectric power factor of 30 μV m−1 K−2. Stretching beyond the yield point as well as repeated tensile deformation and bending leave the electrical properties of these fibers almost unaffected. The mechanical robustness/durability and excellent underwater stability of semicrystalline PEDOT:PSS fibers, combined with a promising thermoelectric performance, opens up their use in practical energy‐harvesting textiles, as illustrated by an embroidered thermoelectric fabric module.