No abstract

This study demonstrates the full infiltration of gel polymer electrolyte into silicon-coated vertically aligned carbon nanofibers (Si-VACNFs), a high-capacity 3D nanostructured anode, and the electrochemical characterization of its properties as an effective electrolyte/separator for future all-solid-state lithium-ion batteries. Two fabrication methods have been employed to form a stable interface between the gel polymer electrolyte and the Si-VACNF anode. In the first method, the drop-casted gel polymer electrolyte is able to fully infiltrate into the open space between the vertically aligned core-shell nanofibers and encapsulate/stabilize each individual nanofiber in the polymer matrix. The 3D nanostructured Si-VACNF anode shows a very high capacity of 3450 mAh g(-1) at C/10.5 (or 0.36 A g(-1)) rate and 1732 mAh g(-1) at 1C (or 3.8 A g(-1)) rate. In the second method, a preformed gel electrolyte film is sandwiched between an Si-VACNF electrode and a Li foil to form a half-cell. Most of the vertical core-shell nanofibers of the Si-VACNF anode are able to penetrate into the gel polymer film while retaining their structural integrity. The slightly lower capacity of 2800 mAh g(-1) at C/11 rate and ∼1070 mAh g(-1) at C/1.5 (or 2.6 A g(-1)) rate have been obtained, with almost no capacity fade for up to 100 cycles. Electrochemical impedance spectroscopy does not show noticeable changes after 110 cycles, further revealing the stable interface between the gel polymer electrolyte and the Si-VACNFs anode. These results show that the infiltrated flexible gel polymer electrolyte can effectively accommodate the stress/strain of the Si shell due to the large volume expansion/contraction during the charge-discharge processes, which is particularly useful for developing future flexible solid-state lithium-ion batteries incorporating Si-anodes.

The SnO2@C@GS composites as a new type of 3D nanoarchitecture have been successfully synthesized by a facile hydrothermal process followed by a sintering strategy. Such a 3D nanoarchitecture is made up of SnO2@C core-shell nanospheres and nanochains anchored on wrinkled graphene sheets (GSs). Transmission electron microscopy shows that these core-shell nanoparticles consist of 3-9 nm diameter secondary SnO2 nanoparticles embedded in about 50 nm diameter primary carbon nanospheres. Large quantities of core-shell nanoparticles are uniformly attached to the surface of wrinkled graphene nanosheets, with a portion of them further connected into nanochains. This new 3D nanoarchitecture consists of two different kinds of carbon-buffering matrixes, i.e., the carbon layer produced by glucose carbonization and the added GS template, leading to enhanced lithium storage properties. The lithium-cycling properties of the SnO2@C@GS composite have been evaluated by galvanostatic discharge-charge cycling and electrochemical impedance spectroscopy. Results show that the SnO2@C@GS composite has discharge capacities of 883.5, 845.7, and 830.5 mA h g(-1) in the 20th, 50th and 100th cycles, respectively, at a current density of 200 mA g(-1) and delivers a desirable discharge capacity of 645.2 mA h g(-1) at a rate of 1680 mA g(-1). This new 3D nanoarchitecture exhibits a high capability and excellent cycling and rate performance, holding great potential as a high-rate and stable anode material for lithium storage.

A study on the development of high-power supercapacitor materials based on formation of thick mesoporous MnO2 shells on a highly conductive 3D template using vertically aligned carbon nanofibers (VACNFs). Coaxial manganese shells of 100 to 600 nm nominal thicknesses are sputter-coated on VACNFs and then electrochemically oxidized into rose-petal-like mesoporous MnO2 structure. Such a 3D MnO2/VACNF hybrid architecture provides enhanced ion diffusion throughout the whole MnO2 shell and yields excellent current collection capability through the VACNF electrode. These two effects collectively enable faster electrochemical reactions during charge-discharge of MnO2 in 1 M Na2SO4. Thick MnO2 shells (up to 200 nm in radial thickness) can be employed, giving a specific capacitance up to 437 F g(-1). More importantly, supercapacitors employing such a 3D MnO2/VACNF hybrid electrode illustrate more than one order of magnitude higher specific power than the state-of-the-art ones based on other MnO2 structures, reaching ∼240 kW kg(-1), while maintaining a comparable specific energy in the range of 1 to 10 Wh kg(-1). This hybrid approach demonstrates the potential of 3D core-shell architectures for high-power energy storage devices.