In the present work, PPy, ZnO, and polypyrrole/zinc oxide (PPy/ZnO) microcomposites (1, 2, and 5 wt%) were prepared and their properties have been tuned for anticorrosion applications on low carbon mild steel. The synthesized products: ZnO, PPy, and composites were characterized by various sophisticated analytical techniques such as XRD, FTIR, Raman, FESEM, EDX, UV–VIS, TGA, and BET. The band frequencies observed at 480 and 588 cm−1 in FTIR spectrum correspond to stretching vibrations of Zn‐O and N‐H bonds, respectively, broadening of the bands in the composites indicate strong interactions between ZnO and PPy matrix. The potentiodynamic polarization study of PPy and PPy/ZnO composite was carried out in 3.5% NaCl solution to investigate the corrosion resistance efficiency. PPy/1 wt% ZnO (Icorr = 190 nA) composite coating on low carbon mild steel was observed to exhibit best corrosion protection property compared to PPy (121 μA), 2 and 5 wt% ZnO (242, 295 nA) composites. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 48319.

ZnO and halide (Cl, Br, and I) enriched ZnO samples have been synthesized by polyol method. Halide enriched zinc oxide (ZnO-X) were obtained when synthesis was carried out in the presence of tetrabutylammonium halide (X-Cl, Br, and I) salts. X-ray results reveal that the halide ions seem to occupy the oxygen vacancy sites as well as interstitial sites of the ZnO lattice increasing the cell volume and strain along the c-axis. Microspheres are observed in the scanning electron micrographs with the size ranging between 170 and 385 nm. Photocatalytic activity of the synthesized samples was tested under UV light irradiation for the decomposition of Rhodamine-6G dye.The halide enriched ZnO samples show higher rate of dye degradation compared to pristine ZnO attributable to their higher bandgap leading to a decrease in the recombination reactions of the electron-hole pair and higher light absorbing ability. ZnO-Br is seen to exhibit the highest rate of degradation due to higher bandgap, light absorbing ability and predominance of (101) facet in the lattice. Further, ZnO-Br appears to undergo negligible change after 3 cycles of catalysis proving its reusability.