The construction industry in addition to being considered one of the biggest natural resources consumers is still responsible for generating large quantities of residues. The impacts caused by these residues have motivated research aimed at developing new techniques for reuse and recycling this material by using as raw material to make alternative materials. The introduction of demolition residues (DR) in soil-lime bricks replacing part of the pozzolan becomes possible due to the cementing properties that these residues may present when finely grounded. This study aims to evaluate the durability of soil-lime blocks embedded with demolition residues. For this study the raw materials were characterized by particle size distribution analysis, X-ray diffraction and chemical analysis. Then test specimens were prepared using mixes in a 1:10 ratio of lime:soil and embedded with residue in partial replacement of lime, in the proportions of 25%, 50% and 75% with curing period of 90 days. Later, the test specimens were evaluated for durability. The results showed that soil-lime bricks embedded with contents above 50% of residues had their durability affected.

Novas técnicas vêm sendo desenvolvidas com o objetivo de incentivar o desenvolvimento sustentável e tentar minimizar a degradação ambiental causada pela extração indiscriminada de recursos naturais além da constante geração de resíduos de construção e demolição. Esta pesquisa objetiva avaliar a utilização de resíduos da construção civil, oriundos de demolição, como agente pozolânico na fabricação de blocos solo-cal. As matérias primas convencionais e alternativas (resíduos) foram caracterizados por meio dos seguintes ensaios: massa especifica real, área específica, análise granulométrica por peneiramento e por difração á laser,limites de liquidez e plasticidade, análise química e difração de raios X. Para os ensaios tecnológicos foram confeccionados corpos de prova solo-cal no traço 1:10 em peso, com substituição da cal por resíduos nas seguintes proporções: 0, 10, 20, 25, 30, 40, 50 e 75%. Os corpos de prova foram curados por períodos de 28, 60 e 90 dias, em câmara úmida com 100% de umidade relativa, em seguida determinada sua resistência à compressão simples e absorção de água. Com os melhores resultados de resistência a compressão simples, foram moldados blocos solo-cal e solo-cal-resíduo. Os resultados obtidos com os blocos solo-cal incorporados com resíduo evidenciaram valores dentro das especificações das normas da ABNT, apontando que existe viabilidade técnica no aproveitamento de resíduos de demolição para uso na fabricação de blocos solo-cal sem função estrutural.

The volume of waste generated by mining and mineral processing industries has escalated each day because of increased demand caused by global economic growth. The kaolin processing industries are important economic segments in the state of Paraiba, but generate huge amounts of waste. An alternative for the recycling of this waste is its use in mortars. The kaolin contained in wastes after thermal treatment can reduce the consumption of cement in the production of mortars. It was evaluated the influence of firing temperatures of the residue on its pozzolanic activity. The residue was fired at temperatures of 600°C, 700°C and 800°C for 2h and subjected to mineralogical analysis. The evaluation produced the mortar with a mixture of kaolin waste burned at temperatures of 600°C, 700°C and 800°C with lime delivering true a good mechanical performance, reaching values of compressive strength greater than the legislated.

A incorporação dos resíduos de demolição da construção civil (RD) em tijolos solo-cal, substituindo parte do aglomerante, torna-se possível devido às propriedades cimentantes que esses resíduos podem apresentar quando finamente moídos. Essa pesquisa objetiva avaliar a durabilidade de tijolos solo-cal incorporados com resídu-os de demolição da construção civil. Para o desenvolvimento dessa pesquisa foram confeccionados corpos-de-prova utilizando o traço 1:10 em massa, em proporção de cal:solo e incorporados com resíduo em substituição parcial à cal, nas proporções de 25%, 50% e 75%, para períodos de cura de 28, 60 e 90 dias. Posteriormente, os corpos-de-prova foram submetidos à avaliação da durabilidade. Os resultados obtidos mostraram que a incorporação do resíduo aos tijolos solo-cal em teores superiores a 50% reduz sua durabilidade. Palavras-chave:Solo-cal, resíduos de demolição e durabilidade. Abstract The introduction of demolition residues (DR) into soil-lime bricks

The use of agricultural waste has become a necessity due to the high environmental cost derived from its improper disposal in nature. In this scenario, rice husks, as well as the ash produced by burning, became worrying in certain regions of the country due to the large volume produced annually [.