No abstract

Although Ru catalysts supported on reducible oxides such as TiO 2 hold significant promise for the deoxygenation of biomass derived oxygenates, a significant drawback is their instability under oxidation conditions necessary for catalyst regeneration. In this contribution, the role of TiO 2 crystal structure on resistance to metal particle sintering during calcination treatments at 400 and 500 °C is investigated. The resulting impact of the calcination temperature and TiO 2 support phase for the conversion of guaiacol at 400 °C under atmospheric pressure of hydrogen over supported Ru catalysts is presented. Results suggest that the rutile TiO 2 phase plays an important role in stabilizing Ru particles during calcination pretreatment in comparison with anatase supported Ru catalysts. Furthermore, rates normalized to the area of the support and the Ru suggest that the high activity of Ru/TiO 2 systems for guaiacol conversion is attributed to defect sites created by hydrogen spillover from the Ru metal to the reducible TiO 2 as opposed to only the sites located at the Ru/TiO 2 interface. † Electronic supplementary information (ESI) available. See

No abstract

The process and energy intensifications for the synthesis of glycerol carbonate (GC) from glycerol and dimethyl carbonate (DMC) using an eggshell-derived CaO heterogeneous catalyst were investigated. The transesterification reaction between glycerol and DMC was typically limited by mass transfer because of the immiscible nature of the reactants. By varying the stirring speed, it was observed that the mass transfer limitation could be neglected at 800 rpm. The presence of the CaO solid catalyst made the mass transport-limited reaction process more prominent. Mass transfer intensification using a simple kitchen countertop blender as an alternative to overcome the external mass transfer limitation of a typical magnetic stirrer was demonstrated. A lower amount of the catalyst and a shorter reaction time were required to achieve 93% glycerol conversion or 91% GC yield, and the turnover frequency (TOF) increased almost 5 times from 1.5 to 7.2 min−1 when using a conventional magnetic stirrer and countertop blender, respectively. In addition, using a simple kitchen countertop blender with 7200 rpm, the reaction temperature of 60 °C could be reached within approximately 3 min without the need of a heating unit. This was the result of the self-frictional heat generated by the high-shear blender. This was considered to be heat transfer intensification, as heat was generated locally (in situ), offering a higher homogeneity distribution. Meanwhile, the trend toward energy intensification was promising as the yield efficiency increased from 0.064 to 2.391 g/kJ. A comparison among other process intensification techniques, e.g., microwave reactor, ultrasonic reactor, and reactive distillation was also rationalized.

Waste eggshell is proposed as a highly active catalyst for glycerol carbonate production from dimethyl carbonate (DMC) and glycerol. The effect of reaction temperature, reaction time and catalyst loading on the reaction performance were investigated in order to find a suitable operating condition. CaO derived from waste eggshell exhibits catalytic activity comparable to commercial CaO. By using CaO eggshell, glycerol conversion of 96% can be achieved within 90 min of reaction time under 2.5:1 feed molar ratio of DMC to glycerol, 0.08 mole ratio of CaO to glycerol and reaction temperature of 60°C. The catalyst was examined by XRD, TGA/DSC, SEM, N2 adsorption-desorption and Hammett indicators method. Utilization of eggshell as a catalyst for glycerol carbonate production not only provides a cost-effective and value-added of waste eggshell as a green catalyst, but also decrease amount of waste and its treatment cost which is ecologically friendly.