In situ time-resolved X-ray absorption fine structure spectra of Pt/C, Pt3Co/C, and Pt3Ni/C cathode electrocatalysts in membrane electrode assemblies (catalyst loading: 0.5 mgmetal cm–2) were successfully measured every 100 ms for a voltage cycling process between 0.4 and 1.0 V. Systematic analysis of in situ time-resolved X-ray absorption near-edge structure and extended X-ray absorption fine structure spectra in the molecular scale revealed the structural kinetics of the Pt and Pt3M (M = Co, Ni) bimetallic cathode catalysts under polymer electrolyte fuel cell operating conditions, and the rate constants of Pt charging, Pt–O bond formation/breaking, and Pt–Pt bond breaking/re-formation relevant to the fuel cell performances were successfully determined. The addition of the 3d transition metals to Pt reduced the Pt oxidation state and significantly enhanced the reaction rates of Pt discharging, Pt–O bond breaking, and Pt–Pt bond re-forming in the reductive process from 1.0 to 0.4 V.

The degradation of Pt electrocatalysts in membrane electrode assemblies (MEAs) of polymer electrolyte fuel cells under working conditions is a serious problem for their practical use. Here we report the kinetics and mechanism of redox reactions at the surfaces of Pt/C and Pt3Co/C cathode electrocatalysts during catalyst degradation processes by an accelerated durability test (ADT) studied by operando time-resolved X-ray absorption fine structure (XAFS) spectroscopy. Systematic analysis of a series of Pt LIII-edge time-resolved XAFS spectra measured every 100 ms at different degradation stages revealed changes in the kinetics of Pt redox reactions on Pt/C and Pt3Co/C cathode electrocatalysts. In the case of Pt/C, as the number of ADT cycles increased, structural changes for Pt redox reactions (charging, surface, and subsurface oxidation) became less sensitive because of the agglomeration of catalyst particles. It was found that their rate constants were almost constant independent of the agglomeration of the Pt electrocatalyst. On the other hand, in the case of Pt3Co/C, the rate constants of the redox reactions of the cathode electrocatalyst gradually reduced as the number of ADT cycles increased. The differences in the kinetics for the redox processes would be differences in the degradation mechanism of these cathode electrocatalysts.